The Distribution and Morphology of Trace Mg at A Grain-Boundary in A Ni-Base Superalloy

J ZHU,ZY CHENG,HQ YE

DOI: https://doi.org/10.1016/0036-9748(89)90124-5

1989-01-01

Scripta Metallurgica

Abstract:1.1. The Mg is concentrated around the grain boundary, especially at the incoherent interface between the carbide and the matrix (or y′-phase) to form a small Laves phase Ni 2Mg, which is of about 20nm size. This Laves phase makes the boundary rich in Mg, the flank of the carbide smooth, the depleted zone effectively shrink and the density of vacancies at the grain boundary decrease From Table 1 it seems that the small Laves phase Ni 2Mg (about 10nm size) does not damage the ductility but does improve the high temperature creep fracture toughness.2.2. It has never been reported before that any intermetallic NiMg phase exists in a Ni-base superalloy with a such low percentage (0.005wt.%) of Mg. The reason is that the spatial resolution is so poor in conventional experimental methods, that the diffraction intensity and other information from the small NiMg particles are much less than what can be observed. However microdiffraction and microanalysis is a potentially powerful tool for the investigation of the very fine scale microstructure.