Abstract:Polycarbosilane (PCS) serves as a crucial precursor for silicon carbide (SiC) fibers and ceramics. However, both of the precursor and the resulting SiC ceramics are carbon-rich, which is often viewed as detrimental to their relevant high-temperature properties. In this work, PCS is modified using nanosized Si particles to improve SiC grain growth and reduce carbon content in the resulting SiC ceramics, and the structural evolution during the polymer–ceramic conversion process has been meticulously investigated. The findings reveal that the incorporation of nano-Si into PCS raises its actual ceramic yield and accelerates the organic-inorganic conversion process. This is attributed to the formation of a more crosslinked structure at 200 °C–350 °C, resulting from the reaction between the Si–OH groups in nanosized Si and the Si–H and Si–CH3 groups in PCS. The carbothermic reaction between nano-Si and the free carbon starts at approximately 1200 °C at the periphery of nanosized Si particles, and is accomplished at around 1400 °C. This leads to the formation of large-sized reactive β-SiC. Simultaneously, PCS-derived β-SiC with smaller sizes is also formed at 1300 °C–1400 °C. At 1600 °C–1800 °C, the growth of the reactive and the derived β-SiC in nano-Si-modified PCS is both accelerated due to a substantial decrease in the free carbon content. Consequently, the grain size of β-SiC is much larger than that of unmodified PCS. Additionally, the residual amorphous free carbon transforms into nanocrystalline carbon at around 1400 °C and evolves into graphite carbon at 1600 °C–1800 °C, which exhibits a more ordered structure with larger size compared to that in unmodified PCS.

Synthesis and Characterization of SiC(Ti) Ceramics Derived from a Hybrid Precursor of Titanium-Containing Polycarbosilane

A linear polycarbosilane containing <i>m</i>-carborane units: Synthesis and characterization as precursor for SiC/B<sub>4</sub>C ceramics

Synthesis of Polytitanocarbosilane and Preparation of Si–C–Ti–B Fibers

A linear polycarbosilane containing m-carborane units: Synthesis and characterization as precursor for SiC/B4C ceramics

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

Preceramic Polymer As Precursor for Near‐stoichiometric Silicon Carbon with High Ceramic Yield

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process

Fabrication and characterization of SiC–TiB 2 composite ceramics used as infrared source material

Novel Synthesis of (hf 0.25 Zr 0.25 Ti 0.25 Ta 0.25 )C-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Novel Synthesis of (Hf0.25zr0.25ti0.25ta0.25)c-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Polymethylsilane As A Precursor to High-Purity Silicon-Carbide

Self-propagating high temperature combustion synthesis of TiC/TiB2 ceramic–matrix composites

Synthesis of Poly-Titanosilazanes and Conversion into Si3n4-Tin Ceramics

Preparation and Stereolithography of SiC Ceramic Precursor with High Photosensitivity and Ceramic Yield

Preparation and Characterization of Pure SiC Ceramics by High Temperature Physical Vapor Transport Induced by Seeding with Nano SiC Particles

High-performance Ti composites reinforced with in-situ TiC derived from pyrolysis of polycarbosilane

Preparation and Characterization of Pure SiC Ceramics by HTPVT Induced by Seeding with SiC Nanoarrays

Polymer-derived SiC/B4C/C nanocomposites: Structural evolution and crystallization behavior

Preparation of SiC ceramic fiber from a photosensitive polycarbosilane

Enhanced Mechanical/electrical Properties of in Situ Synthesized SiC-TiB2 Ceramic Composites by Reactive Hot-Pressing Sintering