Abstract:Continuous SiC fiber is a kind of high–performance ceramic fiber that combines many advantages, such as high strength, high modulus, high hardness and low density. It has excellent mechanical properties, high–temperature and oxidation resistance, which could be applied as essential reinforcement in advanced ceramic matrix composites (CMCs) in the fields of aerospace and advanced weaponry. Melt–spinnable polytitanocarbosilane (PTCS) is an important precursor, which can be used to prepare continuous SiC fibers through a precursor–derived method. In this work, low–softening–point polycarbosilane (LPCS) and tetrabutyl titanate were used to prepare polytitanocarbosilane with a ceramic yield of 67.5 wt% at 1000 °C. FT–IR, TGA, GPC, 1H NMR, 29Si NMR, and elemental analysis were used to analyze the composition and structure of the PTCS precursor. Finally, Si–C–Ti–B fibers with an average tensile strength of 1.93 GPa were successfully prepared by melt spinning, pre–oxidation, pyrolysis, and high–temperature sintering of the PTCS precursor. The strength retention rates were 71.5% and 79.8% after heat treatment at 1900 °C and 2000 °C under an argon atmosphere for 1 h, respectively. The strength retention rates of Si–C–Ti–B fibers are higher than those of commercial Hi–Nicalon fibers, Tyranno ZMI fibers and Hi–Nicalon S fibers. This work can lay a theoretical foundation and technical support for developing high-performance SiC ceramic fibers containing titanium and their ceramic matrix composites.

High-performance Ti composites reinforced with in-situ TiC derived from pyrolysis of polycarbosilane

Low Volume Fraction in Situ (ti5si3+ti2c)/ti Hybrid Composites with Network Microstructure Fabricated by Reaction Hot Pressing of Ti–SiC System

Microstructure and tribological properties of titanium matrix composites reinforced with in situ synthesized TiC particles

In-situ formed TiCx reinforced Ti composites derived from polyzirconocarbosilane precursor: Synthesis, characterization and mechanical properties

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Fabrication of an In-Situ Ti-2.6vol%Tic Metal Matrix Composite by Thermomechanical Consolidation of A Tih2-1vol%Cnts Powder Blend

Microstructure, mechanical properties and strengthening mechanisms of in-situ prepared (Ti5Si3 + TiC0.67)/TC4 composites

Microstructure and Compressive Properties Ofin SituSynthesized TiC/Ti Composites

Strengthening and toughening of Ti 5 Si 3 by TiC-coated short carbon fiber: Fabrication, interfacial control, and mechanism of reinforcement

Microstructure and compressive properties of in situ synthesized (TiB + TiC)/Ti composites

Achieving high strength and superior wear‐resistant properties in TiH2 matrix reinforced with graphene nanoplates

Micron-sized SiC Particles Reinforced TC4 Composites: Mechanical Properties and Strengthening Mechanisms

In situ synthesis and mechanical properties of bulk Ti3SiC2/TiC composites by SHS/PHIP

Synthesis of Polytitanocarbosilane and Preparation of Si–C–Ti–B Fibers

Strengthening Effects of Tic Particles and Microstructure Refinement in in Situ Tic-Reinforced Ti Matrix Composites

In-situ synthesis and superhigh modulus of network structured TiC/Ti composites based on diamond-Ti system

Microstructure and Mechanical Properties of in Situ Synthesised (Tic+tib)/ti-6Al-4v Composites Prepared by Powder Metallurgy

Microstructure And Compressive Properties Of In Situ Synthesized (Tib Plus Tic)/Ti Composites

Microstructure and tensile properties of in situ synthesized (TiBw + TiCp)/Ti6242 composites

Microstructural characterization and mechanical properties of (TiC+TiB)/TA15 composites prepared by an in-situ synthesis method

Effect of TiC Content on Microstructure and Mechanical Properties of High-temperature Titanium Matrix Composites