Abstract:A low-density, high-specific surface area, high-strength and large-sized carbon aerogel preparation process is a key technology in the industrial application of aerogel science. In recent years, ingenious nanostructure design, along with salt templates, drying optimization and other strategies have been applied by numerous scientists. As a result, the specific surface area of carbon aerogel has significantly increased and the density reduced. However, the preparation of high-strength and large-sized intact carbon aerogel at low cost is still a challenge due to the limitations of thermal treatment equipment and drying process. In this study, we propose an improved preparation method of ambient pressure solvothermal polymerization and auxiliary ambient pressure drying by the principle of acid–base two-step catalysis using resorcinol and furfural as raw materials. Resultantly, the condensation and cross-linking reaction process is stabilized by the ambient pressure solvothermal polymerization, which effectively reinforces the interfacial bonding between primary particles and forms a high-strength skeleton. The breaking strength of the aerogels reach up to 9.74 MPa. The auxiliary ambient pressure drying can greatly reduce the drying shrinkage and density of the aerogel and solve the problems of drying deformation and cracking of large-sized carbon aerogel. The drying shrinkage and density of the obtained carbon aerogels are reduced to 3.22% and 0.203 g/cm 3 , respectively, and the specific surface area reaches 675.057 m 2 /g. Moreover, the large-sized sample (70 mm (d) × 25 mm (h)) can also be prepared by this method since the strength of skeleton can resist the capillary force of pore structure, and the nanoporous architecture can be perfectly retained. Therefore, this study provides a new preparation scheme for the industrial large-scale production and application of carbon aerogel.

Preparation of Cresol–formaldehyde Carbon Aerogels Via Drying Aquagel at Ambient Pressure

PREPARATION OF MONOLITHIC CARBON AEROGELS FROM M-CRESOL WITH FOEMALDEHYDE THROUGH SOL-GEL PROCESS

Preparation of Carbon Aerogels at Room Temperature Using Acetonitrile As Solvent

Control of Mesoporous Structure of Aerogels Derived from Cresol-Formaldehyde

Carbon aerogels derived from cresol–resorcinol–formaldehyde for supercapacitors

Characterization of the microstructures of organic and carbon aerogels based upon mixed cresol–formaldehyde

Preparation of Carbon Aerogels by Conventional Drying

Preparation of Silica Aerogels Via Non-supercritical Drying and Their Formation Process

Preparation and Microstructure Control of Carbon Aerogels Produced Using M-Cresol Mediated Sol-Gel Polymerization of Phenol and Furfural

Synthesis of Monolithic Carbon Aerogels with High Mechanical Strength Via Ambient Pressure Drying Without Solvent Exchange

PREPARATION AND CHARACTERIZATION OF ORGANIC AEROGELS FROM CRESOL MIXTURE WITH FORMALDEHYDE

Organic and Carbon Aerogels from the NaOH‐catalyzed Polycondensation of Resorcinol–furfural and Supercritical Drying in Ethanol

Preparation of Carbon Aerogels by Conventional Drying and Their Control in Microstructure

Preparation of Low-Density Carbon Aerogels by Ambient Pressure Drying

Preparation of Silica Aerogels by Non-Supercritical Drying

The preparation of carbon aerogels based upon the gelation of resorcinol–furfural in isopropanol with organic base catalyst

Low-density, high-strength and large-scaled monolithic carbon aerogels fabricated via modified ambient pressure drying

Carbon Aerogel Films Synthesized at Ambient Conditions

Low-density organic and carbon aerogels from the sol–gel polymerization of phenol with formaldehyde

Preparation of Monolithic Carbon Aerogels and Investigation of Their Pore Interconnectivity by a Nanocasting Pathway

Preparation of mesoporous carbon aerogels via ambient pressure drying using a self-sacrificing melamine-formaldehyde template