Abstract:Silica aerogel has been formed using CO2 gas as the gelation agent through the low-cost ambient pressure drying technique. With water wash and the following solvent exchange process for Na+ removal, this synthesis route has no ion exchange resin used and becomes more straightforward. In order to reduce the silica particle and pore sizes, different hydrolysis-condensation rate control agents including dimethylformamide (DMF), methyl-triethoxysilane (TMES), Glycerol and methyltrimethoxylsilane (MTMS) have been applied to modify the structural groups of silica network. Results show that MTMS is the most effective control agent and the optimized MTMS/silica sol volume ratio has been found at 1% by testing the specific surface area of the aerogel. In addition, the effects of chlorotrimethylsilane (TMCS) amount and the calcining temperature on the physicochemical properties of the aerogel have been also investigated. When the TMCS/silica sol volume ratio is 0.4, Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) measurement shows that there is an apprent exothermic peak at calcining temperture of 420 degrees C, caused by the transformation of Si-CH3 group to Si-OH group. X-ray photoelectric spectroscopy (XPS) results show that the percentages of Si-C(-H) bonds with binding energy of 102.4 eV have decreased from 25.5% to 7.2% after 420 degrees C calcining. The contact angle of the as-dried aerogel is as high as 154 and dramatically decreases to ca. 109 degrees after calcining at 450 degrees C. The pore volume and BET specific surface area both increase first and then decrease with the increase of calcining temperature, and the pore volume reaches the maxmium of 1.45 cm(3)/g at 400 degrees C and it confirms Si-CH3 group release. This study offers a new facile route to the synthesis of silica aerogel and presents a promising way of the cost-effective large-scale manufacturing.

Preparation of mesoporous carbon aerogels via ambient pressure drying using a self-sacrificing melamine-formaldehyde template

Monolithic carbon aerogels within foam framework for high-temperature thermal insulation and organics absorption

Low-density, high-strength and large-scaled monolithic carbon aerogels fabricated via modified ambient pressure drying

Strong and machinable carbon aerogel monoliths with low thermal conductivity prepared via ambient pressure drying

Synthesis of carbon aerogels with controlled morphology and pore structure to modulate their bulk density and thermal conductivity via a quick one-pot preparation strategy

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Facile preparation of lightweight and robust carbon aerogel monoliths for high-temperature thermal insulation and oil-water separation

Preparation of the methyltriethoxysilane based aerogel monolith with an ultra-low density and excellent mechanical properties by ambient pressure drying

Synthesis and Characterization of MF Aerogels

Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Transparent, Ultraflexible, and Superinsulating Nanofibrous Biocomposite Aerogels Via Ambient Pressure Drying

Facile Synthesis Of Methylsilsesquioxane Aerogels With Uniform Mesopores By Microwave Drying

Chemical Foaming Coupled Self-Etching: A Multiscale Processing Strategy for Ultrahigh-Surface-Area Carbon Aerogels.

Synthesis of alumina aerogel enriched carboxymethyl cellulose with polymodal pore size distribution by ambient pressure drying

Molecular design of polymer precursors for controlling microstructure of organic and carbon aerogels

A Facile Strategy for Freeze-Drying Preparation of Silica Aerogel from Sodium Silicate

Organic solvents-free and ambient-pressure drying melamine formaldehyde resin aerogels with homogeneous structures, outstanding mechanical strength and flame retardancy

Preparation and Microstructure Control of Carbon Aerogels Produced Using M-Cresol Mediated Sol-Gel Polymerization of Phenol and Furfural

A scalable molecular-templating strategy toward well-defined microporous carbon aerogels for efficient water treatment and electrocatalysis

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Synthesis of Porous and Mechanically Compliant Carbon Aerogels Using Conductive and Structural Additives