Abstract:The effect of pre-ageing deformation on the size and distribution of beta-prime precipitates and subsequently on the resulting strength and ductility have been measured in a Mg-3.0at.%Zn-0.5at.%Y alloy. The alloy was extruded and then subjected to a T8 heat treatment comprised of a solution-treatment, cold-work and artificial ageing. Extrusion was used to introduce texture, ensuring that deformation occurred via slip rather than twinning. Samples were subjected to controlled uniaxial deformation and then isothermally aged to peak hardness. Precipitate length, diameter and number density were measured and evaluated in terms of the strength and ductility of the alloy. The nucleation of the beta-prime precipitates in peak-aged condition without pre-ageing deformation (i.e.T6 treatment) was poor, with only 0.5% volume fraction, compared to approximately 3.5% in T6 treated binary Mg-3.0at.%Zn alloy. The microstructure of the Mg-Zn-Y alloy was less refined, with larger diameter precipitates and lower beta-prime number densities compared to a binary Mg-3.0at.%Zn alloy. Deformation to 5% plastic strain increased the volume fraction of beta-prime precipitates to approximately 2.3% and refined the beta-prime precipitate length and diameter. The combination of these effects increased the yield strength after isothermal ageing from 217MPa (0% cold-work) to 287 MPa (5% cold-work). The yield stress increased linearly with reciprocal interparticle spacing on the basal and prismatic planes and the alloy showed similar strengthening against basal slip to Mg-Zn. The elongation increased linearly with particle spacing. The ductility of Mg-Zn-Y alloys was similar to that of Mg-Zn for equivalently spaced particles.

Effect of precipitates on microstructures and properties of forged Mg-10Gd-2Y-0.5Zn-0.3Zr alloy during ageing process

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Effect of Y on Age Hardening Response and Mechanical Properties of Mg-xY–1.5LPC −0.4zr Alloys

Precipitate evolution of as-cast Mg-9Gd-2Y-0.5Zn-0.5Zr alloy containing LPSO, β′′, β′ and γ'' phases during isothermal aging at 200 °C

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Static recrystallization and precipitation behavior of forged and annealed Mg–8.7Gd–4.18Y–0.42Zr magnesium alloy

Precipitation Behavior of Mg-7Gd-3Y-2Zn-0.5Zr Alloy during Isothermal Aging

The Aging Behaviour of a Mg-10Gd-3Y-1.0Zn-0.5Zr (wt.%) Alloy with Long-Period Stacking Ordered Phase at 275°C

Characterization of precipitates in aged Mg-4 wt%Zn alloy

On precipitation hardening behaviour in a triaxial forged Mg-2Zn-2Gd alloy and relationship to mechanical properties

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Precipitate Evolution in Mg−7Gd−3Y−1Nd−1Zn−0.5Zr Alloy During Isothermal Ageing at 240 °C

The effect of precipitation on strength and ductility in a Mg-Zn-Y alloy

Maximizing precipitation hardening effect enables ultrahigh strength in a coarse-grained Mg-13Gd forging alloy

Influence of Solution Treatment Time on Precipitation Behavior and Mechanical Properties of Mg-2.0Nd-2.0Sm-0.4Zn-0.4Zr Alloy

A Preliminary Study on the Effects of Aging Temperature on the Microstructure and Mechanical Properties of As-Extruded Mg-12Gd-4Y-1Zn Magnesium Alloy

Effect of aging time on discontinuous precipitates, continuous precipitates and mechanical properties of AZ80A magnesium alloy

Weak Strengthening Effect of the Precipitated Lamellar Phase in the Homogenized Mg-8Gd-4Y-1.6Zn-0.5Zr (wt%) Alloy Followed by Furnace Cooling

Effects of heat treatment on mechanical properties of an extruded Mg-4.3Gd-3.2Y-1.2Zn-0.5Zr alloy and establishment of its Hall–Petch relation