Abstract:In order to investigate the effect of heat treatment on the microstructure and tensile properties of an Mg-5Gd-4Y-0.5Zn-0.5Zr alloy, the phase diagram was calculated by Pandat software, and accordingly the as-extruded alloy was annealed at 450, 510 and 550 °C followed by water quenching. The microstructure and mechanical properties of the specimens were analyzed subsequently by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and tensile testing. The results showed that the average grain size of the as-extruded specimen was about 4 μm, in which Mg24Y5 was detected, and fine-grain strip was formed during the extrusion process. The grain size of the specimen annealed at 450 °C for 24 h was about 11 μm, and the main secondary phases were 14H-LPSO, δ-Zr3Zn2, β1-Mg3Gd and (HCP)Zr particles. The plate-like 14H-LPSO and cubic β1- Mg3Gd phases were coherent with the matrix, and the surface layer of (HCP)Zr was enriched with Zn atoms. When the annealing temperature reached 510 °C and 550 °C, the grain size increased to about 83 and 151 μm, respectively. The 14H-LPSO phases were gradually dissolved while the other secondary phases still existed. It was shown by uniaxial tensile testing that the ultimate tensile strength (UTS), yield tensile strength (YTS) and elongation (EL) of the as-extruded specimen were 291 MPa, 236 MPa and 24.7%, respectively. Increase of UTS, EL and decrease of YTS was resulted after annealed at 450 °C. However, both the strength and ductility dropped obviously after annealed at 510 °C and 550 °C. Ductile fracture features were found on the fracture surface of the as-extruded and 450 °C annealed specimens, whereas brittle topology, such as cleavage, was the main feature on the fracture surfaces of the specimens annealed at higher temperatures. Based on the strength analysis, it was concluded that the fine-grain strengthening was more important than solution strengthening and precipitation strengthening in this work.

Static recrystallization and precipitation behavior of forged and annealed Mg–8.7Gd–4.18Y–0.42Zr magnesium alloy

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Dynamic precipitation during multi-axial forging of an Mg–7Gd–5Y–1Nd–0.5Zr alloy

Deformation-induced Dynamic Precipitation of 14H-LPSO Structure and Its Effect on Dynamic Recrystallization in Hot-Extruded Mg-Y-Zn Alloys

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Dynamic Recrystallization, Texture Evolution, and Improved Mechanical Properties of Mg-Y-Zn-V Alloy during Forging and Subsequent Extruding Deformation

Tuning texture and precipitation using Y/Gd atomic ratio in iso-concentration Mg–Y–Gd–Ag–Zr extruded alloys

Maximizing precipitation hardening effect enables ultrahigh strength in a coarse-grained Mg-13Gd forging alloy

Effect of Annealing on Microstructure and Tensile Properties of As-Extruded Mg-5Gd-4Y-0.5Zn-0.5Zr Alloy

Precipitation Behavior of Mg-7Gd-3Y-2Zn-0.5Zr Alloy during Isothermal Aging

Dynamic Recrystallization Mechanism and Precipitation Behavior of Mg-6Gd-3Y-3Sm-0.5Zr Alloy During Hot Compression

Effect of Gd content on microstructure and dynamic mechanical properties of solution-treated Mg−xGd−3Y−0.5Zr alloy

Excellent isotropic mechanical properties of directed energy deposited Mg-Gd-Y-Zr alloys via establishing homogeneous equiaxed grains embedded with dispersed nano-precipitation

On precipitation hardening behaviour in a triaxial forged Mg-2Zn-2Gd alloy and relationship to mechanical properties

Effect of Deformation Parameters on Recrystallization Behavior and Long-Period Stacking-Ordered Phase of Mg-9Gd-4Y-2Zn-0.5Zr Alloy

Dynamic nano precipitation behavior of as-cast Mg-4Li-4Zn-Y alloy during high temperature deformation

Effect of Cold Forging and Static Recrystallization on Microstructure and Mechanical Property of Magnesium Alloy AZ31

Microstructure and Phase Transformation of Forged Mg–3.7Zn–0.3Y–0.3Gd Quasicrystal Alloy

Effect of Y and Gd solutes on grain refinement of the as-extruded Mg-Gd(-Y)-Zn-Mn alloys