Characterization of precipitates in aged Mg-4 wt%Zn alloy

Yuping Ren,Boshu Liu,Hongbo Xie,Hongxiao Li,Min Jiang,Gaowu Qin
DOI: https://doi.org/10.1016/j.mtcomm.2021.102017
IF: 3.8
2021-03-01
Materials Today Communications
Abstract:<p>The precipitation phases play a critical role in affecting the properties of age-hardenable Mg alloys. The structure and morphology of the intragranular and intergranular precipitates in aged Mg-4 wt%Zn alloy were investigated by using transmission electron microscope (TEM) and high resolution TEM (HRTEM). The peak hardness of 62 HV was obtained after the alloy was aged at 150 °C for 200 h. The precipitates were composed of a large amount of <span class="math"><math>β1′</math></span> and very low amount of <span class="math"><math>β2′</math></span> and β. The diameter and length of <span class="math"><math>β1′</math></span> rods were in the range of 15−20 nm and over 1.3 μm, respectively. The structure of <span class="math"><math>β1′</math></span> was hexagonal close-packed (HCP) MgZn<sub>2</sub> instead of Mg<sub>7</sub>Zn<sub>4</sub>. The orientation relationship between <span class="math"><math>β1′</math></span> and Mg matrix was <span class="math"><math>21¯1¯0β1'//0002Mg</math></span> and <span class="math"><math>0001β1'//21¯1¯0Mg</math></span>. The oval shaped precipitate with triclinic Mg<sub>3</sub>Zn<sub>2</sub> structure appeared preferentially at the grain boundary. Its size and morphology did not show much difference with an increase in the aging time. The thin and long <span class="math"><math>β1′</math></span> rods dominated the strengthening effect of Mg-Zn alloy.</p>
materials science, multidisciplinary
What problem does this paper attempt to address?