Abstract:In this study, NiCrSiB-SiC composite coatings were prepared on 16Mn low-carbon steel by vacuum cladding technology using SiC and NiCrSiB mixed powders as raw materials for enhancing their wear resistance. The effects of different content of SiC particles on the microstructure evolution, mechanical and abrasive wear properties of the coatings were investigated. The results showed that SiC particles in all the NiCrSiB-SiC composite coatings with different SiC contents were completely decomposed into C and Si under the catalysis of Ni-based alloy. The out-diffused Si into the coating mainly led to the formation of the Ni 3 Si eutectic phase, while the out-diffused C introduced M 7 C 3 , M 3 C 2 , M 2 (C, B) and other hard phases. Besides, C also diffused to the substrate, leading to a carburizing effect, which remarkably enhanced the mechanical properties of the substrate. In the NiCrSiB-SiC composite coatings with high SiC content, the decomposition of SiC led to the remaining graphite phase. However, once the concentration of SiC was over high, excess graphite would deteriorate the compactness and adhesion of the coating, weakening its wear performance. The nanoindentation and abrasive wear experiments revealed that the composite coating with 5 wt% SiC particles had lower elastic modulus ( E ), higher hardness ( H ), H / E , and H 3 / E 2 , and its wear volume was only 1/10 of that of the substrate, indicating the best mechanical and wear properties. The excellent wear performance can be attributed to the combination of the in-situ formed carbides and borides hard reinforcing phases and the tough coating matrix composed of Fe and Si dissolved γ-Ni and Ni 3 Si eutectic phase.

Influences of Nickel Infiltration in C/SiC Composite on Its Thermophysical Properties

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Properties of Carbon Nano-Tubes–cf/sic Composite by Precursor Infiltration and Pyrolysis Process

High strength C/Si‒Ni‒C composites fabricated by reaction melt infiltration with Si‒Ni alloy at lower temperature

Microstructure evolution, mechanical and abrasive wear properties of NiCrSiB-SiC composite coatings prepared on 16Mn low-carbon steel by Ni-based alloy catalyzed SiC decomposition

Effect of Nickel Element Diffusion on the Tribological Properties of Cemented Carbide Materials under High Temperature Condition

Wetting Behaviors of Nickel-Based Alloys on Sintered Silicon Carbide Ceramics

Effects of Ni content and sintering temperature on the microstructure and mechanical properties of TiC-Ni composites fabricated by selective carburization of Ti-Ni alloys

Electrochemical deposition and tribological behaviour of Ni and Ni–Co metal matrix composites with SiC nano-particles

Influence of Ni content on the microstructure and mechanical properties of chromium carbide-nickel composites

Effect of Ni content on the wear behavior of Al-Si-Cu-Mg-Ni/SiC particles composites

Thermal Expansion Behavior of Carbon Fiber Reinforced Chemical-Vapor-infiltrated Silicon Carbide Composites from Room Temperature to 1400 °C

Reactions Mechanism and Mechanical Properties of a SiCf/SiC Joint Affected by Cu/Ni/Ti Elements and Inhomogeneous Composites

Mechanical Behavior of Α-Al2o3-coated SiC Particle Reinforced Nickel Matrix Composites

Thermal Analysis of Ni-Cu Alloy Nanocomposites Processed by Sand Mold Casting

Interfacial Reactions and Mechanical Properties Studies of C-Coated and C/B4C Duplex-Coated SiC Fiber-Reinforced Ti2AlNb Composites

Investigation on Microstructure and Properties of the Electrodeposited Ni-SiC Composite Coating

Effect of Α-Al2o3 Coatings on the Interface of Ni/SiC Composites Prepared by Electrodeposition

Microstructure Evolution and Its Effect on the Mechanical Properties of the ZrC–SiC Composite Joint Diffusion Bonded with Pure Ni Foil

Chemical and Wetting Analysis of the Ni-Ti Coating on SiC Improved by a 2-Step Coating-Sintering Process