Abstract:Cordierite honeycomb ceramics are sintered under a range of sintering atmosphere and temperature conditions. The linear thermal expansion coefficient (CTE) is measured along the extrusion direction. The samples sintered in an enclosed crucible have a much lower CTE than those sintered in open air. The CTE decreases with increasing sintering temperature up to 1450 °C. The polymorphic phases, texture, amorphous phase, impurity crystals, and porosity are analyzed using scanning electron microscopy, HR‐TEM, porosimeter, and Rietveld refinement method. The sintered samples consist of two polymorphic phases: indialite (hexagonal symmetry) and cordierite (orthorhombic symmetry). Both the volume % of the cordierite phase and the crystal texture increase with increasing sintering temperature. The orthorhombic distortion of cordierite from the hexagonal lattice (indialite) increases with increasing sintering temperature. The characteristic six‐membered ring of the (Si,Al)‐O4 tetrahedra in the cordierite structure shows substantial changes in the bond length due to Al‐Si ordering. Amorphous phase and impurity crystal phases such as silimanite and spinel remain at temperatures as high as 1450 °C. The effect of the polymorphic phases, the degree of texture, amorphous phase, impurity crystal phases, and the orthorhombic distortion is discussed in relation to the CTE characteristics of honeycomb. The sintered honeycomb consists of two polymorphic phases, indialite (hexagonal symmetry) and cordierite (orthorhombic symmetry). The volume % of cordierite phase and the crystal texture increase with increasing sintering temperature. The thermal expansion coefficient (CTE) reduces with the sintering temperature. The orthorhombic distortion originates from Al‐Si ordering. Amorphous and silimanite phases are ascribed to higher CTEs of the samples sintered in open air.

Synthesis of Cordierite with Low Thermal Expansion Coefficient

A simple method for the preparation of cordierite ceramics with high strength and low thermal expansion coefficient

Mechanism of Cordierite Formation Obtained by High Temperature Sintering Technique

Thermal Expansion Anisotropy of Cordierite Crystal

Direct ink writing of cordierite ceramics with low thermal expansion coefficient

In-situ synthesis and properties of porous cordierite ceramics with adjustable pore structure

Fabrication and Characterization of Porous Cordierite Ceramics Prepared from Fly Ash and Natural Minerals

Preparation of Cordierite Powder by Chemical Coprecipitation–rotation Evaporation and Solid Reaction Sintering

Synthesis and Characterization of Single-Phase α-Cordierite Glass-Ceramics for LTCC Substrates from Tuff

Fabrication of textured cordierite ceramics with low thermal expansion coefficient and custom structure via vat photopolymerization

Effect of Cerium Addition on Phase Transformation and Microstructure of Cordierite Ceramics Prepared by Sol-Gel Method

Effects of Y₂O₃ Additive on Mechanical and Thermal Properties of Cordierite-Mullite Ceramics

Synthesis of Porous Cordierite Using Rice Husk As Silica Source and Pore Forming Agent

Low-temperature preparation of porous cordierite-mullite ceramics using rice husk as silica source and pore-forming agent

Utilization of Sepiolite in the Synthesis of Porous Cordierite Ceramics

Cordierite Material with Increased Heat Resistance

Low-Temperature Combustion Synthesis of Cordierite Ceramic Powder

Crystal Structure and Thermal Expansion Coefficient of Cordierite Honeycomb Ceramics

Synthesis of Cordierite Powders by Low Temperature Combustion Method

Influence of La3+, Ce4+ on phase transition and sintering property of cordierite material prepared by solid reaction

Influence of La_2O_3 on Preparation and Performance of Porous Cordierite from Rice Husk