Abstract:Abundant availability of fly ash due to the combustion of coal in thermal power plants presents a major threat to rising environmental pollution. To preserve the environment, fly ash was explored as the starting material for cordierite synthesis. Cordierite ceramics are widely used in the production of microelectronic components, catalyst substrate material for internal combustion engine. Hence, this research was pursued to fabricate the cordierite in a cost effective manner using fly ash containing the major constituent’s silica (SiO2) and alumina (Al2O3). Cordierite synthesis is carried out using raw materials fly ash, magnesia and dopants such as ZrO2, CeO2 and TiO2 at different composition (5–20 wt%). The properties and the microstructure of prepared samples were evaluated using X-ray diffraction (XRD), thermogravimetric and differential thermal analysis (TG/DTA), and scanning electron microscopy. Their mechanical and thermal properties such as the hardness, the fracture toughness, the flexural strength and the thermal expansion coefficient (CTE) were studied and compared with their morphology. It was found that the hardness, the fracture toughness, and the flexural strength were improved on the addition of the dopant in the cordierite matrix. The cordierite-ZrO2 ceramics (CZr20) exhibited a Vickers hardness value of 7.04 GPa, the fracture toughness of 3.47 MPa m½, and flexural strength of 196.72 MPa. The results confirm the cordierite synthesized with fly ash along with dopants is found suitable for use as catalytic substrate materials with improved mechanical properties.

Cordierite Material with Increased Heat Resistance

Synthesis of Cordierite with Low Thermal Expansion Coefficient

Effects of Y₂O₃ Additive on Mechanical and Thermal Properties of Cordierite-Mullite Ceramics

Effect of high temperature heating on the microstructure and performance of cesium-based geopolymer reinforced by cordierite

A simple method for the preparation of cordierite ceramics with high strength and low thermal expansion coefficient

Effect of Mineral Composition and Sintering Temperature on the Synthetic Cordierite

Nano-Scale Cordierite Glass-Ceramic from Natural Raw Materials with Different Fluoride Additions

Cordierite-Based Ceramics from Coal Fly Ash for Thermal and Electrical Insulations

Preparation, microstructure, and thermophysical properties of Cr3+-modified cordierite high emissivity ceramic for metal thermal protection

Fly Ash Constituent-Silica and Alumina Role in the Synthesis and Characterization of Cordierite Based Ceramics

Preparation of Mullite-Aluminum Titanate-Cordierite Multiphase Ceramics

Porous MgO-based ceramics synthesized by the volume expansion effect: Designing and performance

Experimental Study on Toughening of Porous Cordierite Ceramic Prepared by Particle-Stabilized Emulsions

Elaboration and Chemical Corrosion Resistance of Tubular Macro-Porous Cordierite Ceramic Membrane Supports

In-situ synthesis and properties of porous cordierite ceramics with adjustable pore structure

Thermal Shock and Ablation Behavior of Α-Cordierite Glass-Ceramic Coating on Porous BN/Si2N2O Ceramic

Fabrication and Characterization of Porous Cordierite Ceramics Prepared from Fly Ash and Natural Minerals

Thermal/mechanical properties of cordierite synthesized using coal gangue as a refractory material

An Unusual Carbon–Ceramic Composite with Gradients in Composition and Porosity Delivering Outstanding Thermal Protection Performance Up to 1900 °C

Low-Temperature Combustion Synthesis of Cordierite Powder and Its Characteristic

Formation, Conversion and Elimination of Intermediate Spinel Phase in MgO/kaolin Mixture Firing for Cordierite