Abstract:Assorted morphologies of precipitates in fcc/bcc transformation systems have been reported, which often exhibit irrational characteristic. Various models have been developed to explain the habit plane (or the broad facet), but the overall morphologies of the precipitates are seldom explained quantitatively. In this work, the equilibrium cross-section of rod-shape austenite precipitates in duplex stainless steel is determined by atomistic simulation. The input orientation relationship (OR) between fcc and bcc phase is determined according to the O-line criterion (one of the interfaces contains a single set of dislocations), with the condition that the invariant line lies in close-packed plane pair of (1 (1) over bar(1) over bar)(f)|(10 (1) over bar)(b) and the Burgers vector of O-lines is [011](f|)/2|((1) over bar 11)(b)/2. The obtained OR is close to the K-S OR ((11 (1) over bar)(f)//(01 (1) over bar)(b), [101](f)//(111)(b)), with the deviation of 1.27 degrees from the parallelism in both planes and directions. Interfacial energy of interfaces in various orientations in the zone axis of the invariant line ([0.75 0.10 0.65](f)//[0.52 0.68 0.52](b)) has been calculated. To ensure the reliability of the calculated values, an initial atomic configuration free of interstitial and vacancy is constructed for each interface. The energies of the O-line interface, the interface normal to either Delta g(((1) over bar 11)) or Delta g((020)) are found to have similar values, each at a local minimum. Based on the calculated interfacial energies, the equilibrium cross-section morphology is determined by the Wulff construction. The result shows that the morphology exhibits a near rhombus cross-section, which agrees consistently with experiments. One of the major facets is the O-line interface, normal to ((0.66) over bar 0.12 0.74)(f)//((0.51) over bar (0.24) over bar 0.83)(b), in agreement with the observation. The other facet is normal to Delta g((020)) (((0.25) over bar (0.87) over bar 0.42)(f)//(0.45 (0.73) over bar 0.51)(b)) in the calculated result, while it is normal to Delta g(((1) over bar 11)) (((0.36) over bar (0.77) over bar 0.53)(f)//(0.31 (0.71) over bar 0.63)(b)) in experimental results, with about 10 degrees difference between them. The discrepancy between calculated and observed results is probably because the experiments have not reached the equilibrium state. The dislocation structures in these three interfaces are identified from the atomic simulation results by a newly developed method based on the singular value decomposition of the Nye tensor. It confirms that the O-line interface contains a single set of [011](f)/2 dislocations with spacing of 1.5 nm. The interface normal to either Delta g(((1) over bar 11)) or Delta g((020)) contains two sets of dislocations. The dislocation structure in the facet normal to Delta g((1) over bar 11)) is in good agreement with experimental observation of the non-O-line facet, including the local decomposition of dislocation core to (1 (1) over bar(1) over bar)(f) stacking faults.

Coincidence structures of interfacial steps and secondary misfit dislocations in the habit plane between Widmanstätten cementite and austenite

A New Orientation Relationship Between Cementite and Austenite and Coexistence of Pseudo-Primary and Secondary Dislocations in the Habit Plane

An Extended Near-Coincidence-sites Method and the Interfacial Structure of Austenite Precipitates in a Duplex Stainless Steel

Pitsch and t-h orientation relationships between widmanstatten cementite and austenite

Dislocation description of martensite interfaces based on misfit analysis

Calculation of Interfacial Dislocation Structures: Revisit to the O-lattice Theory

Lattice mismatch and twist partitioning at commensurate dichromatic pattern of two-phase interfaces

Unified rationalization of the Pitsch and T–H orientation relationships between Widmanstätten cementite and austenite

Secondary Dislocation Structures in a Ni–TiN System from the GMS and O-lattice Theory

A Simple Method for Calculating the Possible Habit Planes Containing One Set of Dislocations and Its Applications to Fcc/bct and Hcp/bcc Systems

An Investigation on the Equilibrium Morphology and Interfacial Structures of Pricipitates in Duplex Stainless Steel by Atomistic Simulation

Stepped Interface and Crystal Orientation in the Eutectic Structure of Cu-71.8%Ag Alloy

High Strain Gradient Plasticity Associated with Wedge Indentation into Face-Centered Cubic Single Crystals: Geometrically Necessary Dislocation Densities

Arrangement and Decomposition of Grain Boundary Dislocations: Two-Mode Phase-Field Crystal Simulation

Direct observations of collinear dislocation interaction in a Fe-17.4 Mn-1.50 Al-0.29 C (wt.%) austenitic steel under cyclic loading by in-situ electron channelling contrast imaging and cross-correlation electron backscatter diffraction

A New Mechanism for Misfit Dislocation Generation : Superdislocations Associated with Ruddlesden – Popper Planar Defects

Burton-Cabrera-Frank Theory for the Influence of Off-Cut Direction on the Growth of Hcp Crystals

Drift-Induced Step Instabilities Due to the Gap in the Diffusion Coefficient

A crystallographic model of the {557} habit planes in low-carbon martensitic steels

Revisiting step instabilities on crystal surfaces. Part I: The quasistatic approximation

Interpretation of the Habit Plane of Δ Precipitates in Superalloy Inconel 718