Abstract:SiC/SiC composites, prepared by reactive melt infiltration (RMI), exhibit exceptional properties. However, the presence of residual Si in the composite matrix can significantly compromise their high-temperature mechanical properties. Addressing the issue of high-content residual Si aggregation remains a crucial focus of research in order to fully unlock the application potential of SiC/SiC composites prepared by RMI. In this work, a special porous carbon (C g ) is successfully synthesized and introduced into the porous 2D SiC/SiC composites prepared by CVI. The unique pore structure of the SiC/SiC-C g is thoroughly analyzed, along with its liquid Si infiltration process. The difference in coefficient of thermal expansion (CTE) between SiC and C g can cause thermal stress, which can destory the C g structure. Consequently, the C particles detach from the C g skeleton and react with liquid Si to create SiC. This process effectively separates residual Si and helps alleviate the negative effects of residual Si aggregation. The microstructure and phase distribution of SiC/SiC composites obtained by liquid Si infiltrating different C structures are investigated and compared, and it demonstrates the positive effect of C g on the uniform phase distribution of matrix in the composites. The as-received SiC/SiC composites possess a density of 2.94 g/cm 3 with open porosity of 1.23%, and a flexural strength of 808.7±10.2MPa, a fracture toughness of 25.5±1.8MPa·m 1/2 , a tensile strength of 317.4±12.4MPa and a proportional ultimate stress of 157.33±4.1MPa. Acoustic emission (AE) and digital image correlation (DIC) technology are used to study the special mechanical behavior of composites.

Fabrication of SiCf/SiC Composites by Chemical Vapor Infiltration and Vapor Silicon Infiltration

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

Microstructure, Mechanical Properties and Reaction Mechanism of Kd-1 Sicf/Sic Composites Fabricated by Chemical Vapor Infiltration and Vapor Silicon Infiltration

Microstructure and mechanical properties of SiC fiber/Si-CoSi2 matrix composites fabricated by carbon chemical vapor infiltration and Si alloy melt infiltration process

Fabrication and Mechanical Properties of 3-D Cf/C-SiC-TiC Composites Prepared by RMI

Three-dimensional carbon silicon carbide composites prepared by chemical vapor infiltration

Mechanical Properties and Microstructure of KD-1 SiCf/SiC Composites Fabricated by Vapor Silicon Infiltration

Fabrication and characterization of 2.5D and 3D SiCf/SiC composites

Carbon/silicon Carbide Composites Prepared by Chemical Vapor Infiltration Combined with Silicon Melt Infiltration

Study on the Properties of SiCf/SiC Composites Fabricated by Vapor Silicon Infiltration

Microstructure and Properties of Particle Reinforced Silicon Carbide and Silicon Nitride Ceramic Matrix Composites Prepared by Chemical Vapor Infiltration

Microstructure and Mechanical Properties of Three-Dimensional Carbon/Silicon Carbide Composites Fabricated by Chemical Vapor Infiltration

Mechanical Properties of 3D Fiber Reinforced C/SiC Composites

2.5-DIMENSION SiCf/SiC COMPOSITES FABRICATED BY LOW PRESSURE CHEMICAL VAPOR INFILTRATION

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

The Microstructure and Properties of SiC/SiC-based Composites Fabricated by Low-Temperature Melt Infiltration of Al–Si Alloy

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

3D-SiC decorated with SiC whiskers: Chemical vapor infiltration on the porous 3D-SiC lattices derived from polycarbosilane-based suspensions

Microstructure and Oxidation Resistance of Carbon/silicon Carbide Composites Infiltrated with Chromium Silicide

Microstructure and Mechanical Properties of SiCf/SiC Composite Prepared by Chemical Vapor Infiltration