Abstract:In order to improve the mechanical properties and oxidation resistance of three-dimensional carbon fiber-reinforced silicon carbide composites prepared by Low-pressure chemical vapor infiltration (LCVI), electrodeposition chromium combined with silicon melt infiltration method (CSI) is developed for filling the pores of CVI C/SiC composites with chromium silicide. By this method, not only the large pores between bundles but also the small pores between fibers in a bundle can be filled. In the chemical vapor infiltration process, pyrolytic carbon interfacial layer and silicon carbide matrix layer are deposited on the surface of the carbon fiber. The open porosity of as-received CVI C/SiC is as high as 20%. Then the porous composite is infiltrated with chromium. Finally, the composite is infiltrated with silicon melt to react with chromium in the pores, thereby chromium silicide is in-situ formed and C/SiC–Cr3Si composites with open porosity of 5% is obtained. Compared with CVI C/SiC composites, C/SiC–Cr3Si composites exhibit better mechanical property and oxidation resistance. The room-temperature strength of the C/SiC–Cr3Si is 586MPa, much higher than that of the CVI C/SiC. After the CVI C/SiC–Cr3Si composite is exposed in the flame of burner rig for 20 h at 1300°C, the flexural strength of composite decreases only by 4.3%.

Microstructure, Mechanical Properties and Reaction Mechanism of Kd-1 Sicf/Sic Composites Fabricated by Chemical Vapor Infiltration and Vapor Silicon Infiltration

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

Mechanical Properties and Microstructure of KD-1 SiCf/SiC Composites Fabricated by Vapor Silicon Infiltration

Fabrication of SiCf/SiC Composites by Chemical Vapor Infiltration and Vapor Silicon Infiltration

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Study on the Properties of SiCf/SiC Composites Fabricated by Vapor Silicon Infiltration

Microstructure and Mechanical Properties of Three-Dimensional Carbon/Silicon Carbide Composites Fabricated by Chemical Vapor Infiltration

Effects of the fiber surface characteristics on the interfacial microstructure and mechanical properties of the KD SiC fiber reinforced SiC matrix composites

Microstructure and Oxidation Resistance of Carbon/silicon Carbide Composites Infiltrated with Chromium Silicide

Microstructure and mechanical properties of SiC fiber/Si-CoSi2 matrix composites fabricated by carbon chemical vapor infiltration and Si alloy melt infiltration process

Carbon/silicon Carbide Composites Prepared by Chemical Vapor Infiltration Combined with Silicon Melt Infiltration

Microstructure and Properties of Particle Reinforced Silicon Carbide and Silicon Nitride Ceramic Matrix Composites Prepared by Chemical Vapor Infiltration

Study on Microstructures of 2D and 3D Chemical Vapor Infiltration SiC/SiC Composites

Three-dimensional carbon silicon carbide composites prepared by chemical vapor infiltration

STRUCTURE AND MECHANICAL PROPERTIES OF C/SIC COMPOSITES BY REACTIVE MELT INFILTRATION

MICROSTRUCTURE OF 3D TEXTILE C/PYC/SIC COMPOSITES PREPARED BY CHEMICAL VAPOR INFILTRATION

Mechanical Properties of the SiCf/SiC Composites Reinforced with KD-I and KD-II Fibers Fabricated Assisted by a Microwave Heating Method

Relationships Between the Distribution Manner of Fiber and the Properties of KD-I/SiC Composites

Microstructure and Mechanical Properties of SiCf/SiC Composite Prepared by Chemical Vapor Infiltration

Fabrication and characterization of 2.5D and 3D SiCf/SiC composites

Microstructure and mechanical properties of SiC f /SiC composite prepared by chemical vapor infiltration