Preparation and Electrical Properties of Bi2Zn2/3Nb4/3O7 Thin Films Deposited at Room Temperature for Embedded Capacitor Applications

Xiaohua Zhang,Wei Ren,Peng Shi,M. Saeed Khan,Xiaofeng Chen,Xiaoqing Wu,Xi Yao

DOI: https://doi.org/10.1016/j.ceramint.2011.04.053

IF: 5.532

2011-01-01

Ceramics International

Abstract:Bi2Zn2/3Nb4/3O7 thin films were deposited at room temperature on Pt/Ti/SiO2/Si(100) and polymer-based copper clad laminate (CCL) substrates by pulsed laser deposition. Bi2Zn2/3Nb4/3O7 thin films were deposited in situ with no intentional heating under an oxygen pressure of 4Pa and then post-annealed at 150°C for 20min. It was found that the films are still amorphous in nature, which was confirmed by the XRD analysis. It has been shown that the surface roughness of the substrates has a significant influence on the electrical properties of the dielectric films, especially on the leakage current. Bi2Zn2/3Nb4/3O7 thin films deposited on Pt/Ti/SiO2/Si(100) substrates exhibit superior dielectric characteristics. The dielectric constant and loss tangent are 59.8 and 0.008 at 10kHz, respectively. Leakage current density is 2.5×10−7A/cm2 at an applied electric field of 400kV/cm. Bi2Zn2/3Nb4/3O7 thin films deposited on CCL substrates exhibit the dielectric constant of 60 and loss tangent of 0.018, respectively. Leakage current density is less than 1×10−6A/cm2 at 200kV/cm.