Effects of Dielectric Thickness on Energy Storage Properties of 0.87Batio3-0.13Bi(zn2/3(nb0.85ta0.15)1/3)o3 Multilayer Ceramic Capacitors

Hongxian Wang,Peiyao Zhao,Lingling Chen,Xiaohui Wang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.01.032

IF: 5.7

2020-01-01

Journal of the European Ceramic Society

Abstract:Multilayer Ceramic Capacitors (MLCCs) for energy storage applications require a large discharge energy density and high discharge/charge efficiency. Here, 0.87BaTiO(3)-0.13Bi(Zn-2/3(Nb0.85Ta0.15)(1/3))O-3 (BTBZNT) powders were synthesized via solid-state reactions, and MLCCs with sub-micron grains were fabricated using a two-step sintering method. The BTBZNT MLCCs, which are well-defined relaxor ferroelectrics, possessed relatively high permittivity, dielectric sublinearity, and negligible hysteresis. An AC breakdown strength (BDS) enhancement from 511 to 1047 kV/cm was obtained as the dielectric thickness (D) decreased from 26 to 5 mu m. The strong correlation between BDS and D, described as BDS proportional to D-0.368, agreed well with the general macroscopic theory of thermal breakdown in insulators. The enhanced BDS afforded the BTBZNT MLCCs (D similar to 9 mu m) with excellent energy storage properties with a maximum discharge energy density of 10.5 J/cm(3) and discharge/charge efficiency of 93.7% under a maximum electric field of 1000 kV/cm. The MLCCs also exhibited excellent thermal stability with discharge energy density variation < +/- 5% over a wide temperature range of -50 to 175 degrees C under an electric field of 400 kV/cm. These remarkable performances make BTBZNT MLCCs promising for energy storage applications.