High-temperature BaTiO3-based ternary dielectric multilayers for energy storage applications with high efficiency

Wen-Bo Li,Di Zhou,Wen-Feng Liu,Jin-Zhan Su,Fayaz Hussain,Da-Wei Wang,Ge Wang,Zhi-Lun Lu,Qiu-Ping Wang

DOI: https://doi.org/10.1016/j.cej.2021.128760

IF: 15.1

2021-06-01

Chemical Engineering Journal

Abstract:<p>High-temperature BaTiO₃-based ceramic capacitors have broad application prospects in energy storage devices. However, energy density and efficiency of BaTiO₃-based ceramic capacitors are bottleneck challenges that limit the applications of ceramic capacitors in the vast of industrial applications. To address this issue, it needs to design novel BaTiO₃-based ceramics to elevate the breakdown strength, energy density and efficiency of capacitors. Here, high performance BaTiO₃-based ceramics with breakdown strength of 290 kV cm⁻¹, discharge energy density is more than 2.4 J cm⁻³, energy storage efficiency is achieve 91.5% are achieved in novel ternary system 0.88BaTiO₃-0.12(1-x)Bi(Li_0.5Nb_0.5)O₃-0.12xBi(Mg_0.5Ti_0.5)O₃ (BT-BLN-BMT) (0.2 ≤ x ≤ 0.8) lead-free ceramic. Moreover, 0.88BT-0.12(1-x)BLN-0.12xBMT (x = 0.6) multilayer ceramics capacitors effectively increased breakdown strength and energy density values are more than 500 kV cm⁻¹ and 4.42 J cm⁻³, improved by 488% and 1373% compared with only 85 kV cm⁻¹ and 0.3 J cm⁻³ for the pure BaTiO₃. It maintains high thermal stability in the temperature range from 25 °C to 150 °C. All these results have clearly collaborated the promising future of this novel BaTiO₃-based ceramics in energy storage applications in the future.</p>

engineering, chemical, environmental