Abstract:Hot cracks are notorious defects in casting, welding, and additive manufacturing. Grain boundaries play a key role in hot cracking formation. Still, their effects are often neglected in hot cracking susceptibility predictions, and thus a quantitative picture of hot cracking susceptibility and liquid fracture is still lacking. In this work, we construct a multi-order parameter phase-field model for binary alloy solidification to simulate attractive, neutral, and repulsive grain boundaries in the thin-interface limit. Phase-field simulations of different combinations of grain boundary and bi-crystal growth types are used to obtain solidification path data, which is then used as the input into the Rappaz, Drezet and Gremaud (RDG) model (Rappaz et al., 1999). We study the so-called Λ-shape variation of hot cracking susceptibility as a function of solute concentration, showing that the magnitude of the Λ curve peak shifts to higher values and to lower concentrations as grain boundary energy increases. Meanwhile, the peak magnitude becomes higher and shifts to a higher value and higher concentrations when convergent grain growth is applied. Furthermore, in all cases examined, the corresponding pressure drops predicted for hot cracking exceed the theoretical liquid rupture stress, consistent with experimental observations. These results demonstrate that quantitative phase-field simulations, when coupled with the RDG model, are capable of relatively accurately predicting liquid rapture states relevant to hot cracking since the large disparity between the predicted pressure drop and critical stress of liquid film is eliminated through the consideration of grain boundary effects in the solidification path calculation.

The Study Evolution of Casting Hot Cracks Forecast

Simulation Analysis of Thermal Stress During Casting Process of Large-Sized Alloy Steel Ingot

Study on Hot Crack for the Casting of Bolster and Side Bearer by Numerical Simulation

Hot Cracks in Camshaft Casting: Initiation and Propagation

Numerical simulation analysis of thermal stress fields during solidification of steel casting

Progress in numerical simulation of casting process

Application and development of numerical simulation technology in Casting

Research Progress and Prospects of Hot Cracking and Fluidity of Magnesium Alloys

An Integrated Approach to Study the Hot Tearing Behavior by Coupling the Microscale Phase Field Model and Macroscale Casting Simulations

Research Development of Thermal-Mechanical Numerical Modeling of Casting Stress Field

Analysis on Micro Cracks Defect of Francis Turbine Band Casting Based on Solidification Process Simulation

A Study on the Numerical Simulation of Thermal Stress During the Solidification of Shaped Castings

Computer modeling and prediction of solidified microstructure of casting alloy

Numerical Simulation of Temperature Field and Stress Field for and Axial Crack Analysis of Heavy-wall Centrifugally Cast Hollow Bloom

Hot modeling research on initial solidification behavior in continuous casting

Progress in numerical simulation of solidification process of shaped casting

Review on the Interface Interaction Between the Casting and Mold(Core) in Thermal Stress Analysis of Castings

Hot Cracking Susceptibility Prediction from Quantitative Multi-Phase Field Simulations with Grain Boundary Effects

Numerical simulation on flow and heat transfer in twin roll strip casting and rolling molten pool with side dams vibrating

Study on numerical simulation of mold-filling and solidification processes of shaped casting

Evolution of Surface Crack on Slab During Rough Rolling Using Thermal-Mechanical FEM