Hot Cracks in Camshaft Casting: Initiation and Propagation
Yankang Zhu,Gangqiang Xu,Cangsu Xu,Xiaolu Li,Kangkang Zhou,Yuan Chen,Yuntang Li,Xinsheng Xu,Hui Liu
DOI: https://doi.org/10.1080/13640461.2023.2292842
2024-01-01
International Journal of Cast Metals Research
Abstract:In this paper, a numerical simulation method based on the camshaft casting process and crack expansion was proposed to study the propagation characteristics of casting hot cracks. The dynamic visualisation process of hot crack growth indicates that the formation of hot tear is dominated by opening mode cracks. And during the propagation process, the equivalent stress intensity factor at the crack front first decreases and then increases. Furthermore, the propagation characteristics of the crack under different hot tear initiation conditions were studied by this method. The results reveal that the expansion ability of a hot crack is affected by the equilibrium solidification scale, solidification sequence, and solidification path of the casting. Finally, using the microscopic morphology of the cracks, the semi-quantitative analysis of the elements illustrates that the carbon content decreases sharply at the crack formation site, while manganese and sulphur are relatively rich.