Abstract:Abstract In the present investigation, the closed-cell Al foam was fabricated by friction stir processing (FSP) combined with heat treatment. The influences of process parameters on microstructures of closed-cell Al foam precursor were investigated by optical metallographic microscope and scanning electronic microscope (OM/SEM). Fluent CFD software was developed to simulate the temperature field and flow field in friction stir processing. The cupping test values were compared for base metal and different weld passes. The results show that the welding speeds have little effect on the mixing of powder in the stir zone because of the relatively small welding heat input. However, the pore size and pore morphology are highly sensitive to change in the rotating speeds. When the welding speed is 50mm/min and the rotating speed is 2000rpm, the powder ring is continuous and uniform due to sufficient plastic deformation and flow. When the foaming time is 110s, the expansion rate of the whole foam increases rapidly, and the diameter of the pore is uniform. Numerical simulation shows that the welding heat mainly comes from the shoulder of the stirring head and the welding temperature peak appears near the stirring pin. The maximum flow velocity appears at the outer edge of the shaft shoulder in which the aluminum matrix is softened preferentially. When the rotating speed increases to 2000r/min, the velocity of the outermost edge of the shaft shoulder increases by 59.96%, and the maximum temperature at the stirring pin reaches 491°C which is consistent with the experimental results. The formability of the joint interface is improved. The cupping test values increase with the increase of deformation temperature. Especially the cupping test value of foamed preform is close to that of base metal at 450°C.

Low-Frequency Internal Friction of Foamed Al

RESEARCH ON THE INTERNAL FRICTION OF FOAMED ALUMINIUM IN ACOUSTIC FREQUENCY

Study on Damping Behavior of Foamed Aluminum with Macroscopic Pores

Quasi-static Deformation Mechanism and Compressive Properties of Aluminum Foams Fabricated by Friction Stir Processing

Aluminum Foam Sandwich: Pore Evolution Mechanism Investigation and Engineering Preparing Optimization

Effects of process parameters and alloy compositions on the pore structure of foamed aluminum

Measurement of tortuosity in aluminum foams using airborne ultrasound

Coupling Effect Of Porosity And Cell Size On The Deformation Behavior Of Al Alloy Foam Under Quasi-Static Compression

Solidification Structure and Sound Absorbability of A356 Alloy Foams

Properties of Aluminum Foam Prepared by Gas Injection Method

Dynamic and Static Compression Tests and FEA Analyses of Aluminum Foam Specimen with Variable Density in the Loading Direction

Local deformation on damping performance of integral-forming aluminum foam sandwich

Microstructure and Compressive Properties of Aluminum Foams Made by 6063 Aluminum Alloy and Pure Aluminum

Study on Cell Deformation of Low Porosity Aluminum Foams under Quasi‐Static Compression by X‐Ray Tomography

Fabrication and characterization of aluminum foam reinforced with nanostructured γ-Al2O3 via friction stir process for enhanced mechanical performance

The Influences of Process Parameters on the Preparation of Closed-cell Aluminum foam by Friction Stir Processing

Mechanical Properties of Aluminium Foam and How Density, Temperature, and Strain Rate Affect Dynamic Strain–Stress Relationship

Characterization of as-cast microstructure of aluminum foams by melt foaming method

Effect of Cu and Sn Additions on the Cellular Structure of Al–Si–Mg Alloys Foaming at Low Temperature (≤600 °C)

Numerical investigation of influences of porous density and strain-rate effect on dynamical responses of aluminum foam

Fabrication and Compressive Behavior of Open-Cell Aluminum Foams Via Infiltration Casting Using Spherical CaCl2 Space-Holders