Study on Damping Behavior of Foamed Aluminum with Macroscopic Pores

Wenzheng Zhang

2009-01-01

Abstract:Experiments have been carried out to study the effects of macroscopic open-pores on the damping behavior of foamed commercially pure aluminum(FA).The damping characterization was conducted on a multifunction internal friction apparatus(MFIFA).The FA specimens were prepared by air pressure infiltration process.The size of macroscopic pores is on the order of a millimeter(0.8 and 1.4 mm) and in large proportions,typically up to 76 vol.%.The internal friction(IF) of the FA specimen was measured at different temperatures,different frequencies,and different amplitude dependences.The measured IF shows that FA has a damping capacity which is enhanced in comparison with bulk commercially pure aluminum,increases with increasing porosity,increases with decreasing macropore size,increases with increasing frequency and increases with increasing strain amplitude.The microstructural analysis was performed using transmission electron microscopy(TEM).TEM observations show that moderate density of dislocation substructures exist near the grain boundaries in the FA.In light of IF measurements and microstructural observations,the possible operative damping mechanisms in the FA are the stress concentration and mode conversion around macroscopic pores,the elastic modulus difference between the matrix and the macroscopic pores that results in a marked inhomogeneous stress,inhomogeneous expansion deformation around macroscopic pores.