Abstract:The solidification microstructure of aluminum foams is evidently different from that of bulk aluminum alloys. Generally, a single α-Al grain runs through the entire thickness of a cell-wall, and the grain morphology is irregular. However, the formation mechanism of the special microstructure in aluminum foams is unclear now, and few studies focused on optimizing the microstructure. In this study, grain refinement of aluminum foams by increasing cooling rate and inoculation were carried out, and thermal analysis was used to measure and judge solidification of aluminum foams. Experimental results show that grain refinement can be achieved by the above two methods, and the latter is more effective. The nucleation undercooling of aluminum foams decreases with the increase of Al–5Ti–1B addition. Grains can be well refined even in thin cell walls after inoculation, and the grain morphology changes from irregular to equiaxed. Under the same conditions, α-Al grains of Al foams are smaller than those of the bulk Al alloy, either with or without inoculation. An anisometric growth model of α-Al grains in foamed aluminum melt restricted by surrounding bubbles is proposed. The model shows that: (1) the size of the inhibited nucleation zone (INZ) around growing grains decreases due to the high constitutional undercooling caused by solute enrichment in cell walls, thus grains in cell walls are smaller than those of bulk Al alloy; (2) under normal solidification conditions, the shape of the INZ is irregular. Grains in aluminum foams will replicate contours of cell walls or Plateau borders, presenting irregular shapes. Increasing cooling rates and/or inoculation can reduce the size of INZ and change its shape. The grain morphology will change from irregular to equiaxed under proper conditions.

Microstructure and Compressive Properties of Aluminum Foams Made by 6063 Aluminum Alloy and Pure Aluminum

Foaming Process and Properties of 6063 Aluminum Foams by Melt Foaming Method

Preparation and Compressive Performance of an A356 Matrix Syntactic Foam

Characterization of as-cast microstructure of aluminum foams by melt foaming method

Comparison of Cell Wall Microstructure of Aluminum Foams Produced by Melt Foaming and Gas Injection Foaming Processes

Fabrication and characterization of aluminum foam reinforced with nanostructured γ-Al2O3 via friction stir process for enhanced mechanical performance

The influence of pure Al and hypoeutectic Al Si alloy base materials on the cell structures of aluminum foams produced by gas injection foaming process

Properties of Aluminum Foam Prepared by Gas Injection Method

Effects of process parameters and alloy compositions on the pore structure of foamed aluminum

Fabrication, Processing, Properties, and Applications of Closed-Cell Aluminum Foams: A Review

Quasi-static Deformation Mechanism and Compressive Properties of Aluminum Foams Fabricated by Friction Stir Processing

Micro-CT in the mechanical properties and energy absorption of closed-cell aluminium foam

Solidification Structure and Sound Absorbability of A356 Alloy Foams

Aluminum Foam Sandwich: Pore Evolution Mechanism Investigation and Engineering Preparing Optimization

High temperature and mesostructure effect on aluminum foam compression responses

Compressive behavior and energy absorption analysis of casting skin-wrapped aluminum foams

Foaming Behavior of AlMg4Si8 Matrix and Pure Al Matrix Precursors in Closed Cavities with Different TiH2 Addition Levels

Comparison of Aluminium Foams Prepared by Different Methods Using X-ray Tomography

Microstructural characteristics and mechanical properties of 7075 aluminum alloy foam sandwich panels fabricated via integrated forming and foaming

Solidification microstructure and grain refinement of closed-cell aluminum foams

Study on an Aluminum Foam by Gas Injection Foaming