Abstract:Aluminum foam that is lightweight with high specific strength, high energy absorption and other characteristics can be used in aerospace, transportation, machinery manufacturing and other fields. The PCM method is usually used to prepare closed-cell aluminum foams. The microsized aluminum foams made by this process can solve the non-uniform pore structures caused by liquid drainage during the foaming process of large aluminum foams. The surface morphology and internal pore structure of microsized aluminum foams are affected by the quality of the precursor used for foaming. In this paper, foamable precursors were obtained via either hot rolling or hot extrusion and subsequently foamed. By analyzing the micromorphology and foaming process of the precursor, the influence of the technological method on the macroscopic pore structure of the final aluminum foam was studied. The results show that the aluminum powder particles in the precursor prepared with the hot rolling method had metallurgical bonding, and the outer surface was dense, with almost no porosity and holes in the interior. The microsized aluminum foam obtained after foaming was smooth in appearance, and the internal pore structure was round and uniform. The reason is that during the foaming process of microsize aluminum foam, the foaming agent was evenly distributed in the precursor of the hot rolling process because of its compact structure. During the foaming process, the decomposed gas of the foaming agent will not escape, and the evenly distributed foaming agent tends to nucleate in situ. In the process of rapid foaming, the pressure in the bubble is enough to resist the liquid drainage phenomenon caused by gravity, and the growth direction of the gas core is isotropic, which promotes the foam structure to be more rounded and uniform.

Comparison of Cell Wall Microstructure of Aluminum Foams Produced by Melt Foaming and Gas Injection Foaming Processes

Comparison of Aluminium Foams Prepared by Different Methods Using X-ray Tomography

The influence of pure Al and hypoeutectic Al Si alloy base materials on the cell structures of aluminum foams produced by gas injection foaming process

Microstructure and Compressive Properties of Aluminum Foams Made by 6063 Aluminum Alloy and Pure Aluminum

Characterization of as-cast microstructure of aluminum foams by melt foaming method

Properties of Aluminum Foam Prepared by Gas Injection Method

Study on an Aluminum Foam by Gas Injection Foaming

Effects of cell wall property on compressive performance of aluminum foams

Foaming Process and Properties of 6063 Aluminum Foams by Melt Foaming Method

Preparation of Aluminum Foam by Gas Injection Foaming

Foaming Behavior of Microsized Aluminum Foam Using Hot Rolling Precursor

Factors Influencing Foam Height in Gas Injection Process for Aluminum Foams

Solidification microstructure and grain refinement of closed-cell aluminum foams

Effects of process parameters and alloy compositions on the pore structure of foamed aluminum

Fabrication, Processing, Properties, and Applications of Closed-Cell Aluminum Foams: A Review

Solidification Structure and Sound Absorbability of A356 Alloy Foams

Compressive Performance and Deformation Mechanism of the Dynamic Gas Injection Aluminum Foams

Oxidation Kinetics of Oxide Film on Bubble Surface of Aluminum Foams Produced by Gas Injection Foaming Process

Research on Key Technologies for Batch Preparation of Aluminum Foam Slabs by Melt Foaming Process

Preparation and Compressive Performance of an A356 Matrix Syntactic Foam

Aluminium foam with sub-mm sized cells produced using a rotating gas injector