The Influences of Process Parameters on the Preparation of Closed-cell Aluminum foam by Friction Stir Processing

Qiu Pang,Zhengjian Wu,Zhili Hu

DOI: https://doi.org/10.21203/rs.3.rs-710772/v1

2021-07-21

Abstract:Abstract In the present investigation, the closed-cell Al foam was fabricated by friction stir processing (FSP) combined with heat treatment. The influences of process parameters on microstructures of closed-cell Al foam precursor were investigated by optical metallographic microscope and scanning electronic microscope (OM/SEM). Fluent CFD software was developed to simulate the temperature field and flow field in friction stir processing. The cupping test values were compared for base metal and different weld passes. The results show that the welding speeds have little effect on the mixing of powder in the stir zone because of the relatively small welding heat input. However, the pore size and pore morphology are highly sensitive to change in the rotating speeds. When the welding speed is 50mm/min and the rotating speed is 2000rpm, the powder ring is continuous and uniform due to sufficient plastic deformation and flow. When the foaming time is 110s, the expansion rate of the whole foam increases rapidly, and the diameter of the pore is uniform. Numerical simulation shows that the welding heat mainly comes from the shoulder of the stirring head and the welding temperature peak appears near the stirring pin. The maximum flow velocity appears at the outer edge of the shaft shoulder in which the aluminum matrix is softened preferentially. When the rotating speed increases to 2000r/min, the velocity of the outermost edge of the shaft shoulder increases by 59.96%, and the maximum temperature at the stirring pin reaches 491°C which is consistent with the experimental results. The formability of the joint interface is improved. The cupping test values increase with the increase of deformation temperature. Especially the cupping test value of foamed preform is close to that of base metal at 450°C.