Abstract:Soaking time and loading rate are the two important process parameters for semi-solid powder forming, which are next only to powder temperature. However, there have been few investigations on the influence of soaking time and loading rate on the semi-solid compression of porous material, which is an effective method for studying the deformation characteristics of semi-solid materials and is widely used to optimize the semi-solid forming processes. Therefore, the microstructures, grain size and shape factor, liquid fraction, relative densities and stress–strain curves of Al-4Cu-Mg alloy with a porosity of 30% compacted at different soaking time and loading rates were measured, and the strain rate sensitivity coefficient, the relationship between peak stresses and strain rates, and the processing map were calculated and analyzed. The results indicate that as the soaking time increases, the particle grows and the liquid fraction increases slightly, and the liquid distribution changes from dots in grains to concentrating on grain boundaries in powders, making the relative density increase basically and the peak stress decrease firstly and then increase slowly. Thus, the most suitable soaking time for semi-solid compression is 2 to 5 min. With the loading rate increasing, the particle size reduces first and then increases, the relative density decreases, while the peak stress basically raises, combining the action of powder breakage, grain coarsening and liquid flowing. The peak stress basically has a power relationship with the strain rate, and the processing map can be used to analyze porous semi-solid materials, which are verified to be consistent with the experimental results. Therefore, the optimal semi-solid forming parameters of Al-4Cu-Mg alloy powders are at a deformation rate ranging from 0.6 to 6 mm/s and at a temperature of 860 to 873 K.

Experimental study on micro-scale filling capacity of semi-solid material

Numerical Simulation of Cavity-Filling Procedures for Micro-Pin-fin Array Thixoforming with Semi-Solid A356 Aluminium Alloy

On the Size Effects in Micro/meso Semisolid Extrusion–forging of A356 Aluminum Alloy

Experimental research on fluidity of semi-solid alloy ZL101 mircoextrusion

Experimental study on semi-solid micro-compression of ZL101 alloy

Experimental Study of High-Frequency Vibration Assisted Micro/Mesoscale Forming of Metallic Materials

Experimental study on isothermal micro-extrusion of ZL101 alloy

Hot micro-extrusion experimentation and die design

Taguchi Experimenting Study on Semi-solid Alloy ZL101 for Thixo-forming and Micro-forward-extrusion

Research On Micro-Forming Process Of Aluminum And Its Alloy

Study on Inhomogeneous Material Flow in Microforming

Research on the Plastic Micro-Forming Ability of the Pure Aluminum and LY12 Aluminum Alloy

Development of a Semi-solid Zn-Al Alloy Filler Metal with Globular Grains

Statistical Investigations of Serpentine Channel Pouring Process Parameters on Semi-Solid ZL101 Aluminum Alloy Slurry Using Response Surface Methodology

Experimental investigation on size effect of ZL101 alloy in micro-upsetting

The Effect of Initial Microstructure of A356 Alloys on the Mechanical Behavior in the Semisolid State

An experimental study on the side-opening filling process at the interface between microchannels with different widths

Mechanism of Filling and Feeding of Thin-Walled Structures During Gravity Casting

Influence of Soaking Time and Loading Rate on Semi-solid Compression of Porous Al-4Cu-Mg Alloy

Analysis of the Effects on the Quality of Micro Injection Molded Products

Research on the constitutive relationship of semi-solid ZL201 alloy