Abstract:TiO2 nanocrystallines with a size of 3–7 nm have been synthesized by the sol–gel method with excessive water at a low temperature of about 50°C. The effects of amount of water and pH on the formation of sols and powders containing TiO2 nanocrystallines were investigated by X‐ray powder diffraction (XRD), transmission electron microscopy, and high‐resolution transmission electron microscopy. The results showed that a pure anatase phase was formed at pH 1, in contrast to the formation of particles with a mixture of anatase and brookite phases at pH 2–7. Moreover, at pH 1, the intensity of the XRD peaks and the crystal size increased with increasing water content when the water ratio increased from 40 to 100. Whereas the crystal intensity remained invariant, the crystal size still increased when the water ratio increased from 100 to 400. The photocatalytic activity was also investigated. It was shown that when the water ratio was below 100, the photocatalytic activity increased with increasing water content. Further increase of the water content decreased the photocatalytic activity. The photocatalytic activity decreased with increasing pH. All samples with pH=1 showed better photocatalytic activity than Degussa P25. Mechanisms for the formation of the TiO2 nanocrystalline particles at such a low temperature were also discussed.

Low-Temperature Crystallization of TiO2 Films on Arranged Mono-Layers by Sol-Gel Method

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Preparation of TiO2 Films on Self-Assembled Monolayers by Sol–gel Method

Preparation of TiO2 films under low temperature condition on the glass substrate

Crystallization Behavior and Hydrophilic Performances of V2O5–TiO2 Films Prepared by Sol–gel Dip-Coating

Low-Temperature Preparation of Ag-TiO2 Composite Films and Their Properties

Soft Solution Approach to Prepare Crystalline Titania Films

Low-Temperature Deposition of Bioactive Crystalline Titania Films: Effects of Tantalum

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Effects of Heat-Treatment Temperature on Preparation of the Sol-Gel-Derived Ag/TiO2 Films

Investigation on the Microstructure and Optical Performance of TiO_2 Films by Sol-Gel Method

Effect of the Substrate Temperature on the Crystallization of TiO2 Films Prepared by DC Reactive Magnetron Sputtering

Low Temperature Coating of Anatase Thin Films on Silica Glass Fibers by Liquid Phase Deposition

Anatase TiO2 film with flake crystals prepared by a sol-gel method without high-temperature heat treatment

Crystallization Behaviors of TiO2 Films Derived from Thermal Oxidation of Evaporated and Sputtered Titanium Films

Low‐Temperature Growth of Monolayer Rutile TiO2 Nanorod Films

A Novel Sol-Gel Method for Preparing Favorable Tio2 Thin Film

Effect of the Ag+ to Ag+/TiO2 film on the crystallization structure

Nanocrystalline Titania Made From Interactions Of Ti With Hydrogen Peroxide Solutions Containing Tantalum Chloride

The Effects of Substrate on the Properties of Sol-Gel Derived TiO2 Films

Preparation and Study of Oriented TiO2 Thin Film