Abstract:TiO₂ sol was produced by the sol-gel method through the hydrolysis and the aging of tetrabutyl titanate and the TiO₂ film was obtained by dipping and uniform lifting of the acid-treated and ultrasound-treated clean glass slides into the TiO₂ sol followed by aging, drying, and calcination. The effect of the hydrolysis control agents to the formed sol was researched and the crystalline state, the morphology, and the photocatalytic properties of the products after calcination were characterized. The structural morphology, the contact angles before and after illumination, and the self-cleaning properties of the TiO₂ film were characterized as well. The results showed that by using acetylacetone as the hydrolysis control agent, the formed TiO₂ sol had relatively high stability. The product after the calcination of the TiO₂ sol was of single anatase type with crystalline size of 18-20 nm and it could degrade nearly 100% of methylene blue after 90 min illumination. The formed TiO₂ film is compact, continuous, smooth, and had the properties of super-hydrophilicity (after 30 min illumination due to its contact angle decreasing from 21° to nearly 0°) and anti-fogging capability, which indicated its excellent self-cleaning property.

Preparation of TiO2 Films on Self-Assembled Monolayers by Sol–gel Method

Low-Temperature Crystallization of TiO2 Films on Arranged Mono-Layers by Sol-Gel Method

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Crystallization Behavior and Hydrophilic Performances of V2O5–TiO2 Films Prepared by Sol–gel Dip-Coating

Preparation of TiO2 nanoparticles on the surface of SiO2 in binary liquids

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

The Effects of Substrate on the Properties of Sol-Gel Derived TiO2 Films

Preparation of TiO2 films under low temperature condition on the glass substrate

The Preparation of TiO2 Film by the Sol-Gel Method and Evaluation of Its Self-Cleaning Property

Preparation of Macroporous and Mesoporous Tio2 Film with Various Solvents

Investigation on the Microstructure and Optical Performance of TiO_2 Films by Sol-Gel Method

Soft Solution Approach to Prepare Crystalline Titania Films

Preparation and Study of Oriented TiO2 Thin Film

The Preparation of TiO_(2-x)N_x(0<x<1) Thin Films by Sol-Gel Method and Its Photocatalysis and Hydrophilic Properties

Nanocrystalline Titania Made From Interactions Of Ti With Hydrogen Peroxide Solutions Containing Tantalum Chloride

Preparation and Crystallization Behavior of SiO2-TiO2 Photo-Catalytic Films

Structure and Photocatalytic Properties of TiO2/Perfluorosulfonated Resin Hybrid Films Prepared by Sol-Gel Method

Porous titania films prepared from interactions of titanium with hydrogen peroxide solution

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

TiO2 film photocatalyst prepared by using sol-gel method with TiCl4 as a precursor

Effects of substrate on the properties of sol-gel derived TiO2 films