Abstract:TiO2 nanocrystallines with a size of 3–7 nm have been synthesized by the sol–gel method with excessive water at a low temperature of about 50°C. The effects of amount of water and pH on the formation of sols and powders containing TiO2 nanocrystallines were investigated by X‐ray powder diffraction (XRD), transmission electron microscopy, and high‐resolution transmission electron microscopy. The results showed that a pure anatase phase was formed at pH 1, in contrast to the formation of particles with a mixture of anatase and brookite phases at pH 2–7. Moreover, at pH 1, the intensity of the XRD peaks and the crystal size increased with increasing water content when the water ratio increased from 40 to 100. Whereas the crystal intensity remained invariant, the crystal size still increased when the water ratio increased from 100 to 400. The photocatalytic activity was also investigated. It was shown that when the water ratio was below 100, the photocatalytic activity increased with increasing water content. Further increase of the water content decreased the photocatalytic activity. The photocatalytic activity decreased with increasing pH. All samples with pH=1 showed better photocatalytic activity than Degussa P25. Mechanisms for the formation of the TiO2 nanocrystalline particles at such a low temperature were also discussed.

Anatase TiO2 film with flake crystals prepared by a sol-gel method without high-temperature heat treatment

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

In-Suit Preparation of Cubic Anatase Tio2 Crystals and Its Photocatalysis Property on Rhodamine B

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Crystallization Behavior and Hydrophilic Performances of V2O5–TiO2 Films Prepared by Sol–gel Dip-Coating

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

Characterization of TiO2 film prepared by sol-gel method using Ti(OC4H9)4

Investigation on the Microstructure and Optical Performance of TiO_2 Films by Sol-Gel Method

Preparation and investigation of TiO2 Sol containing nanometer anatase crystalline grains

Preparation and Study of Oriented TiO2 Thin Film

Soft Solution Approach to Prepare Crystalline Titania Films

Microstructure and photocatalysis kinetics of calcination-free TiO2 film

Preparation and Investigation of TiO<sub>2</sub> Sol Containing Nanometer Anatase Crystalline Grains

Preparation of TiO2 films under low temperature condition on the glass substrate

Low-Temperature Crystallization of TiO2 Films on Arranged Mono-Layers by Sol-Gel Method

Structure and Grain-Size Distribution of Tio2/Sio2 Thin Film

Room-temperature preparation and formation mechanism of porous anatase TiO2 film

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Characterization and Properties of Anatase TiO 2 Film Prepared Via Colloidal Sol Method under Low Temperature

Fabrication and Optical Property Study of TiO2 Nanocrystalline Films by Sol-gel Methods