Abstract:TiO2 nanocrystallines with a size of 3–7 nm have been synthesized by the sol–gel method with excessive water at a low temperature of about 50°C. The effects of amount of water and pH on the formation of sols and powders containing TiO2 nanocrystallines were investigated by X‐ray powder diffraction (XRD), transmission electron microscopy, and high‐resolution transmission electron microscopy. The results showed that a pure anatase phase was formed at pH 1, in contrast to the formation of particles with a mixture of anatase and brookite phases at pH 2–7. Moreover, at pH 1, the intensity of the XRD peaks and the crystal size increased with increasing water content when the water ratio increased from 40 to 100. Whereas the crystal intensity remained invariant, the crystal size still increased when the water ratio increased from 100 to 400. The photocatalytic activity was also investigated. It was shown that when the water ratio was below 100, the photocatalytic activity increased with increasing water content. Further increase of the water content decreased the photocatalytic activity. The photocatalytic activity decreased with increasing pH. All samples with pH=1 showed better photocatalytic activity than Degussa P25. Mechanisms for the formation of the TiO2 nanocrystalline particles at such a low temperature were also discussed.

Characterization and Properties of Anatase TiO 2 Film Prepared Via Colloidal Sol Method under Low Temperature

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Low-Temperature Preparation of Ag-TiO2 Composite Films and Their Properties

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Room-temperature preparation and formation mechanism of porous anatase TiO2 film

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Preparation of TiO2 films under low temperature condition on the glass substrate

Low-Temperature Preparation of Macroporous Anatase TiO2 Thin Film and Its Photocatalytic Activity

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

Fabrication and Optical Property Study of TiO2 Nanocrystalline Films by Sol-gel Methods

Sol-Gel Preparation and Optical Properties of Ag Nanoparticle/TiO2 Composite Films

Investigation on the Microstructure and Optical Performance of TiO_2 Films by Sol-Gel Method

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Development of Low Temperature Synthesizing Nano-sized Titania Film

Preparation of Anatase TiO2 Nanocrystalline and Research on Origion of Phase

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

Anatase TiO2 film with flake crystals prepared by a sol-gel method without high-temperature heat treatment

Low‐Temperature Growth of Monolayer Rutile TiO2 Nanorod Films

Temperature dependence of photoluminescence, Raman scattering, and transmittance spectra of anatase Ti1-xFexO2 nanocrystalline films

FILM FORMING CHARACTERISTICS OF ANATASE TIO2 SOL ON VARIOUS SUBSTRATES AND PROPERTIES OF RESULTANT FILM