Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Low-Temperature Preparation of Macroporous Anatase TiO2 Thin Film and Its Photocatalytic Activity

Low-Temperature Preparation of Ag-TiO2 Composite Films and Their Properties

Controllable hydrothermal synthesis, optical and photocatalytic properties of TiO 2 nanostructures

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Study on in-situ Modification of Vinyl Acetate-Acrylate Latex by Anatase TiO2 Sol

Low-temperature fabrication of porous anatase TiO2 film with tiny slots and its photocatalytic activity

Preparation of Anatase-Type TiO_2 Nanoparticals from Ti (SO4)2 Solution under Hydrothermal Conditions and Its Photocatalytic Performance

Room-temperature preparation and formation mechanism of porous anatase TiO2 film

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Low Temperature Synthesis of Few-Layer Titanate Nanobelts on Ti Mesh and the Hot-Water Induced Transformations to Highly Photocatalytic Active Titania Nanorods

A Preparation Method To Obtain Porous Anatase Tio2 Films At Room Temperature

Low-Temperature Deposition of Anatase Thin Films on Titanium Substrates and Their Abilities to Photodegrade Rhodamine B in Water

Low-temperature preparation of TiO2 films and enhancement of their photocatalytic activity by organic semiconductor

Azobenzene-Containing Block Copolymer Templates for Robust Au@TiO2 Nanoporous Network Films Toward Hot-Electron-Mediated Efficient Visible-Light Photocatalysis

Anatase-TiO2 nano-particle preparation with a micro-mixing technique and its photocatalytic performance

Simple preparation of sub-micron mesoporous TiO2 spheres consisting of anatase nanocrystals

One-Step Synthesis Of Bifunctional Tio2 Catalysts And Their Photocatalytic Activity

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Fabrication Of Macroporous Titanium Dioxide Film Using Pmma Microspheres As Template

Low-Temperature Synthesis of Nanostructured TiO2 Particles and Their Photocatalytic Oxidation Activity

Characterization and Properties of Anatase TiO 2 Film Prepared Via Colloidal Sol Method under Low Temperature