Abstract:High purity, spherical anatase nanocrystals were prepared by a modified sol-gel method. Mixing of anhydrous TiO4 with ethanol at about 0 degrees C yielded a yellowish Sol that was transformed into phase-pure anatase of 7.7 nm in size after baking at 87 degrees C for 3 days. This synthesis route eliminates the presence of fine seeds of the nanoscale brookite phase that frequently occurs in low-temperature formation reactions and also significantly retards the phase transformation to rutile at high temperatures. Heating the as-is 7.7 nm anatase for 2 h at temperatures up to 600 degrees C leads to an increase in grain size of the anatase nanoparticles to 32 rim. By varying the calcination time from 2 to 48 h at 300 degrees C, the particle size could be controlled between 12 and 15.3 nm. The grain growth kinetics of anatase nanoparticles was found to follow the equation, D-2 - D-0(2) = k(0)t(m)e((-Ea/RT)) with a time exponent m = 0.286(+/- 9) and an activation energy of E-a = 32 +/- 2 kJ center dot mol(-1). Thermogravimetric analysis in combination with infrared and X-ray photoemission spectroscopies has shown the anatase nanocrystals at different sizes to be composed of an interior anatase lattice with surfaces that are hydrogen-bonded to a wide set of energetically nonequivalent groups. With a decrease in particle size, the anatase lattice volume contracts, while the surface hydration increases. The removal of the surface hydration layers causes coarsening of the nanoparticles.

Preparation of Anatase TiO2 Nanocrystalline and Research on Origion of Phase

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

High Purity Anatase Tio2 Nanocrystals: Near Room-Temperature Synthesis, Grain Growth Kinetics, And Surface Hydration Chemistry

Synthesis and characterization of nanosized anatase TiO2 cuboids

Preparation and Microcosmic Property Study of Titania Nanocrystals and Films

Phase Transformation and Particle Growth in Nanocrystalline Anatase TiO2 Films Analyzed by X-ray Diffraction and Raman Spectroscopy

STUDY ON THE CONTROLLING OF CRYSTALLINE AND THE TRANSFORMATION TEMPERATURE OF NANO-TITANIA POWDER

Low-Temperature Preparation And Characterization Of Nanosized Crystalline Anatase Titania With Titanium Tetrachloride And Acetic Anhydride As Materials

Investigation on technological process of preparation of TiO2 nanocrystal for rutile crystal growth

Mesoporous Structure and Phase Transition of Nanocrystalline TiO2

Synthesis Of Nanocrystalline Anatase Tio2 By Sol-Gel Method

Preparation and Investigation of TiO<sub>2</sub> Sol Containing Nanometer Anatase Crystalline Grains

A Simple Solution-Phase Route for Room-Temperature Synthesis of Mesoporous and Nanocrystalline Anatase Tio2

Preparation and investigation of TiO2 Sol containing nanometer anatase crystalline grains

Hydrothermal Synthesis and Characterization of Nanocrystalline Anatase Titania from Ti(OC<sub>4</sub>H<sub>9</sub>)<sub>4</sub>

Synthesis and surface state studies of nanocrystalline TiO2

Preparation Principle and Crystal Growth Kinetics of Loaded Nanocrystal TiO2

Preparation and Characterization of Nanometer Sized TiO_2 Thin Film Sintered at Low Temperature

Control of Size and Crystal Form of TiO_2 Nanocrystalline Synthesized by Co-flow Diffusion Flames