Abstract:Highly porous and hydrophobic silica aerogel is fabricated using fly ash and trona ore as the starting materials and the cost-effective ambient pressure drying technique. The optimal calcination parameters are determined as temperature of 850°C, holding time of 2h, and the trona ore/fly ash mass ratio of 1.4. The CO2 release mechanism during calcination is proposed and has been verified by the Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) and X-ray fluorescence (XRF) technique. The hydrogel is derived from reacting the calcination mixture with sulphuric acid solution, followed by filtration. The impurities can be effectively removed through water washing and solvent exchange processes. No ion exchange resin is used in this preparation method, and thus it is a safe, inexpensive and much more straightforward process. In order to minimize drying shrinkage, the hydrogel is first transformed into an alcogel by soaking in ethanol, after which the alcogel is surface modified with the hexane/ethanol/trimethylchlorosilane (hexane/ethanol/TMCS) mixture solution. It has been observed that the specific surface area, BJH desorption pore volume, and BJH desorption average pore diameter all first increase and then decrease so that reach to the maximum values once the heat treatment temperature approaches 500°C due to the oxidation of CH3 groups on the silica skeleton surface. The final product presents special characteristics including: (1) high thermal stability for maintaining hydrophobicity up to 476°C, (2) contact angle of the as-dried silica aerogel as high as 151°, (3) silica particle size of ca. 3–6nm, agreeing well with the model as reported, (4) and the 500°C heat treated sample possessing a large specific surface area of 856.2m2/g, a large pore volume of 2.92cm3/g, and a BJH desorption average pore diameter of 17.1nm. The proposed inexpensive approach produces silica aerogel with superior properties and is a scalable-manufacturing method for large-scale industrial production.

Supercritical drying preparation and fractal structure of blue luminescent silica aerogel

Springback effect and structural features during the drying of silica aerogels tracked by in-situ synchrotron X-ray scattering

Photoluminescence and Photoluminescence Excitation of Si Aerogels Prepared by Supercritical Drying

Preparation of C60-doped Silica Aerogels and the Study of Photoluminescence Properties

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

PREPARATION OF FULLERENCE DOPED SILICA AEROGELS AND THE STUDY OF PHOTOLUMINESCENCE PROPERTIES

Structure modification of silica aerogel

Preparation and optical properties of nano-PbS/SiO2 aerogel assemblies

Preparation and Characterization of Monolithic Silica Fiber/Al2O3 Aerogel Composites by Non-Supercritical Drying

From Phase Separation to Nanocrystallization in Fluorosilicate Glasses: Structural Design of Highly Luminescent Glass-Ceramics

Preparation of Alumina Aerogel via Supercritical Method

Preparation and Characterization of Silica-Titania Aerogel Monoliths by Sol-Gel Method

Clean Synthesis of Silver-Silica Aerogels Via Supercritical Drying and Impregnation

Preparation of Silica Aerogels Via Ambient Pressure Drying

Fractal Structure in Silica and Composites Aerogels

The Relationship Between the Silica Wet-Gels Relative Optical Transmittance at 500 Nm and Structural Features of Silica Aerogels

Synthesis and Characterization of Silica Aerogel and Its Composite Materials

Intense Green Luminescence Associated With Two-Fold Coordinated Si In Silica Aerogel Doped With Al3+

A Novel Preparation Process for Thermally Stable Ultrafine Tetragonal Zirconia Aerogel

Transparent Silica Aerogels: Optical and Chemical Design, Controlled Synthesis, and Emerging Applications

A novel low-cost method of silica aerogel fabrication using fly ash and trona ore with ambient pressure drying technique