Abstract:Highly porous and hydrophobic silica aerogel is fabricated using fly ash and trona ore as the starting materials and the cost-effective ambient pressure drying technique. The optimal calcination parameters are determined as temperature of 850°C, holding time of 2h, and the trona ore/fly ash mass ratio of 1.4. The CO2 release mechanism during calcination is proposed and has been verified by the Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) and X-ray fluorescence (XRF) technique. The hydrogel is derived from reacting the calcination mixture with sulphuric acid solution, followed by filtration. The impurities can be effectively removed through water washing and solvent exchange processes. No ion exchange resin is used in this preparation method, and thus it is a safe, inexpensive and much more straightforward process. In order to minimize drying shrinkage, the hydrogel is first transformed into an alcogel by soaking in ethanol, after which the alcogel is surface modified with the hexane/ethanol/trimethylchlorosilane (hexane/ethanol/TMCS) mixture solution. It has been observed that the specific surface area, BJH desorption pore volume, and BJH desorption average pore diameter all first increase and then decrease so that reach to the maximum values once the heat treatment temperature approaches 500°C due to the oxidation of CH3 groups on the silica skeleton surface. The final product presents special characteristics including: (1) high thermal stability for maintaining hydrophobicity up to 476°C, (2) contact angle of the as-dried silica aerogel as high as 151°, (3) silica particle size of ca. 3–6nm, agreeing well with the model as reported, (4) and the 500°C heat treated sample possessing a large specific surface area of 856.2m2/g, a large pore volume of 2.92cm3/g, and a BJH desorption average pore diameter of 17.1nm. The proposed inexpensive approach produces silica aerogel with superior properties and is a scalable-manufacturing method for large-scale industrial production.

Preparation of silica aerogel from rice hull ash by supercritical carbon dioxide drying

Preparation of silica aerogel from rice hull ash by drying at atmospheric pressure

Synthesis of high specific surface area silica aerogel from rice husk ash via ambient pressure drying

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

A Facile Strategy for Freeze-Drying Preparation of Silica Aerogel from Sodium Silicate

Synthesis and characterization of silica aerogels by a novel fast ambient pressure drying process

Preparation and Characterization of Hydrophobic Silica Aerogel by Ambient Pressure Drying Method

Preparation of Silica Aerogels Via Ambient Pressure Drying

A novel low-cost method of silica aerogel fabrication using fly ash and trona ore with ambient pressure drying technique

Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Robust Silica–Agarose Composite Aerogels with Interpenetrating Network Structure by in Situ Sol–Gel Process

Preparation of Alumina Aerogel via Supercritical Method

Rapid synthesis of sodium silicate based hydrophobic silica aerogel granules with large surface area

Effect of sodium bicarbonate solution on methyltrimethoxysilane-derived silica aerogels dried at ambient pressure

Preparation of Low Density Hydrophobic Silica Aerogels by Controlling Strength of Alcogels

Preparation of superhydrophobic and flexible polysiloxane aerogel

Convenient and rapid preparation of aerogels dried at ambient pressure

Cellulose Aerogels from Aqueous Alkali Hydroxide–Urea Solution

Preparation of Silica Aerogels Monoliths from Hydrophobic Silica Gels and Pluronic10R5 via Sol–Gel Process

Preparation of Hydrophobic Silica Aerogels from Industrial Water Glass