Abstract:New Cu-based bulk glassy alloys were formed in Cu–Zr–Ti and Cu–Hf–Ti systems by the copper mold casting method. The critical diameter is 4 mm for the Cu60Zr30Ti10 and Cu60Hf25Ti15 alloys which are larger than 1 mm for the Cu60Zr40 and Cu60Hf40 glassy alloys. The substitution of Zr or Hf for Ti causes an increase in the glass-forming ability (GFA). As the Ti content increases, the glass transition temperature (Tg), crystallization temperature (Tx), and the supercooled liquid region ΔTx(=Tx−Tg) decrease for both Cu60Zr40−xTix and Cu60Hf40−xTix alloys. In contrast, the liquid temperature (Tl) has a minimum value of 1127 K for the Cu60Zr20Ti20 alloy and 1175 K for the Cu60Hf20Ti20 alloy, resulting in a maximum Tg/Tl of 0.63 and 0.62, respectively. The alloys with the highest Tg/Tl value showed the highest GFA for these Cu-based alloys. The bulk glassy alloys exhibit high tensile fracture strength of 2000–2160 MPa, compressive fracture strength of 2060–2150 MPa and compressive plastic elongations of 0.8–1.7%. The finding of the new Cu-based bulk glassy alloys with high GFA, high fracture strength above 2000 MPa and distinct plastic elongation is encouraging for the future development of a new type of bulk glassy alloy which can be used for structural materials.

A Bulk Glassy Cu–Zr–Ti–Sn Alloy with Superior Plasticity

Crystallization-aided extraordinary plastic deformation in nanolayered crystalline Cu/amorphous Cu-Zr micropillars

Enhanced Plasticity in a Zr-based Bulk Metallic Glass Containing Nanocrystalline Precipitates

A Plastic Zr–Cu–Ag–Al Bulk Metallic Glass

Homogeneity of the Superplastic Zr64.13Cu15.75Ni10.12Al10 Bulk Metallic Glass

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

In‐Situ Precipitated Nanocrystal Beneficial to Enhanced Plasticity of Cu‐Zr Based Bulk Metallic Glasses

Deformation behavior of Zr-based bulk nanocrystalline amorphous alloys

Preparation of (ti0.45cu0.378zr0.10ni0.072)100−xsnx Bulk Metallic Glasses

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

A New Ti–Zr–Hf–Cu–Ni–Si–Sn Bulk Amorphous Alloy with High Glass-Forming Ability

Homogeneous plastic deformation in a Cu-based bulk amorphous alloy

Ni- and Be-free Zr-based bulk metallic glasses with high glass-forming ability and unusual plasticity.

Tensile Elastic Behavior of A Zr-Cu-Ag-Al Bulk Metallic Glass

New Class of Plastic Bulk Metallic Glass.

Unusual Plasticity of the Particulate-Reinforced Cu-Zr-Based Bulk Metallic Glass Composites

Unusual Solidification Behavior of a Zr–Cu–Ni–Al Bulk Glassy Alloy Made from Low-Purity Zr

High Tensile Plasticity and Strength of a CuZr-based Bulk Metallic Glass Composite

Fe-Based Bulk Metallic Glass with High Plasticity