Fabrication of Dense LaCrO3-based Interconnect Thin Membrane on Anode Substrates by Co-Firing

Songlin Wang,Yingchao Dong,Bin Lin,Jianfeng Gao,Xingqin Liu,Guangyao Meng

DOI: https://doi.org/10.1016/j.materresbull.2009.07.001

IF: 5.6

2009-01-01

Materials Research Bulletin

Abstract:In order to develop cost-effective method to prepare ceramic interconnect membrane for solid oxide fell cell stacks, the triple-phase composites of NiO/Sm0.2Ce0.8O2−δ/La0.7Ca0.3Cr0.97O3−δ with the weight ratios of 6:4:x (x=0, 2, 3, 4, 5) were, respectively prepared, and then examined as novel anode supports. The sintering character, microstructure, electrical conductivity, fracture strength, and thermal expansion coefficient of the anodes were, respectively investigated in detail as a function of La0.7Ca0.3Cr0.97O3−δ content. Results indicate the above-mentioned performances of NiO/Sm0.2Ce0.8O2−δ/La0.7Ca0.3Cr0.97O3−δ anode at x≤3 have no significant reduction, and are still acceptable for the practical requirements for solid oxide fell cells. Furthermore, by using a simple and cost-effective drop-coating/co-firing process, dense La0.7Ca0.3Cr0.97O3−δ interconnect membrane was successfully prepared on the anode support of NiO/Sm0.2Ce0.8O2−δ/La0.7Ca0.3Cr0.97O3−δ at x=3. This work presents a simple technical route for developing dense interconnect membranes for Sm0.2Ce0.8O2−δ-based fuel cell stacks.