Novel Composite Interconnecting Ceramics La0.7Ca0.3CrO3−δ/Ce0.8Sm0.2O1.9 for Solid Oxide Fuel Cells

Xiaoliang Zhou,Feijun Deng,Mingxing Zhu,Guangyao Meng,Xingqin Liu

DOI: https://doi.org/10.1016/j.materresbull.2006.11.004

IF: 5.6

2007-01-01

Materials Research Bulletin

Abstract:In this paper, an interconnecting ceramic for solid oxide fuel cells was developed, based on the modification from La0.7Ca0.3CrO3−δ by addition of Ce0.8Sm0.2O1.9. It is found that addition of small amount Ce0.8Sm0.2O1.9 into La0.7Ca0.3CrO3−δ dramatically increased the electrical conductivity. For the best system, La0.7Ca0.3CrO3−δ+5wt.% Ce0.8Sm0.2O1.9, the electrical conductivity reached 687.8Scm−1 at 800°C in air. In H2 at 800°C, the specimen with 3wt.% Ce0.8Sm0.2O1.9 had the maximal electrical conductivity of 7.1Scm−1. With the increase of Ce0.8Sm0.2O1.9 content the relative density increased, reaching 98.7% when the Ce0.8Sm0.2O1.9 content was 10wt.%. The average coefficient of thermal expansion at 30–1000°C in air increased with Ce0.8Sm0.2O1.9 content, ranging from 11.12×10−6 to 12.46×10−6K−1. The oxygen permeation measurement illustrated a negligible oxygen ionic conduction, indicating it is still an electronically conducting ceramic. Therefore, this material system will be a very promising interconnect for solid oxide fuel cells.