Ba0.5Sr0.5Co0.8Fe0.2O3 - δ + LaCoO3 composite cathode for Sm0.2Ce0.8O1.9-electrolyte based intermediate-temperature solid-oxide fuel cells

Wei Zhou,Zongping Shao,Ran Ran,Pingying Zeng,Hongxia Gu,Wanqin Jin,Nanping Xu

DOI: https://doi.org/10.1016/j.jpowsour.2007.03.041

IF: 9.2

2007-01-01

Journal of Power Sources

Abstract:A novel Ba0.5Sr0.5Co0.8Fe0.2O3−δ+LaCoO3 (BSCF+LC) composite oxide was investigated for the potential application as a cathode for intermediate-temperature solid-oxide fuel cells based on a Sm0.2Ce0.8O1.9 (SDC) electrolyte. The LC oxide was added to BSCF cathode in order to improve its electrical conductivity. X-ray diffraction examination demonstrated that the solid-state reaction between LC and BSCF phases occurred at temperatures above 950°C and formed the final product with the composition: La0.316Ba0.342Sr0.342Co0.863Fe0.137O3−δ at 1100°C. The inter-diffusion between BSCF and LC was identified by the environmental scanning electron microscopy and energy dispersive X-ray examination. The electrical conductivity of the BSCF+LC composite oxide increased with increasing calcination temperature, and reached a maximum value of ∼300Scm−1 at a calcination temperature of 1050°C, while the electrical conductivity of the pure BSCF was only ∼40Scm−1. The improved conductivity resulted in attractive cathode performance. An area-specific resistance as low as 0.21Ωcm2 was achieved at 600°C for the BSCF (70vol.%)+LC (30vol.%) composite cathode calcined at 950°C for 5h. Peak power densities as high as ∼700mWcm−2 at 650°C and ∼525mWcm−2 at 600°C were reached for the thin-film fuel cells with the optimized cathode composition and calcination temperatures.