Synthesis and characterization of PrBaCo 2 − x Ni x O 5 + δ cathodes for intermediate temperature SOFCs
Lan Liu,Ruisong Guo,Chao Wang,Chao Zhang,Yuexia Yang,Shanshan Wang
DOI: https://doi.org/10.1007/s10008-014-2534-8
IF: 2.747
2014-01-01
Journal of Solid State Electrochemistry
Abstract:Nickel-substituted layered perovskite PrBaCo 2 − x Ni x O 5 + δ (PBCN) powders with various proportions of nickel ( x = 0, 0.1, 0.2, and 0.3, abbreviated as PBCN-0, PBCN-1, PBCN-2, and PBCN-3, respectively) are investigated as potential cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFCs) based on the yttria-stabilized zirconia (YSZ) electrolyte. It is found that PBCN-1 has the highest electrical conductivity of 1,397 S cm −1 at 400 °C. Substitution of Co by Ni decreases the thermal expansion coefficient (TEC) clearly. The average TEC at the temperature range of 35–900 °C decreases from 22.8 × 10 −6 K −1 for PBCN-0 to 18.9 × 10 −6 K −1 for PBCN-3. The polarization resistances of PBCN samples on YSZ electrolyte at 800 °C are 0.053, 0.048, 0.052, and 0.042 Ω cm 2 for PBCN-0, PBCN-1, PBCN-2, and PBCN-3, respectively. The single fuel cell with the configuration of PBCN-3/YSZ/Pt delivers the highest power densities of 100, 185, 360, 495, and 660 mW cm −2 at 600, 650, 700, 750, and 800 °C, respectively.