Abstract:Ti(C0.7,N0.3)-Mo2C–Ni cermets are fabricated by powder metallurgy methods. We systematically investigate the microstructure, fracture morphology, crack propagation mechanism, and interface characteristics of Ti(C, N)-based cermets with different Ni binder contents.The increased dissolution of carbides and carbonitrides leads to a large amount of (Mo,Ti)(C,N) solid solution precipitates, which then spontaneously nucleate, resulting in a significant increase in the content of white core-gray rim grains in the cermets with a high binder content. The increased Ni binder largely improves the flexural strength and fracture toughness of the Ti(C,N)-based cermets because of the ductile dispersion toughening. The rim-core interfaces have a superior atomic coherent relationship in all Ti(C,N)-based cermets owing to the small lattice mismatch. The lattice mismatch of the interface between the rim phase and metal binder is remarkably decreased with the increase in the binder content to construct an atomic coherent relationship. Thus, the increased Ni binder promotes atomic ordering at the interface between the ceramic grains and binder and strengthens the grain boundary. The characteristic (111) peak of nickel shifts to a larger angle due to the reduction in the Ni-based solid solution lattice distortion. Therefore, the effect of solid solution strengthening is diminished with the increase in binder content, which results in a decreased binder strength. In the Ti(C,N)-based cermets with low metal binder contents, the fracture of the grain boundary between the ceramic grains and binder is the predominant failure mechanism. The intergranular crack accompanied by crack branching is the main characteristic of crack propagation. A hybrid fracture mode of intergranular and transgranular cracks is observed in the Ti(C,N)-based cermets with a moderate binder content. As the binder content further increases, the plastic yield deformation and subsequent tearing of the metal binder are the main fracture characteristics because of grain boundary strengthening and decreased strength of the binder.

Effect of metallic binder content on the microhardness of TiCN-based cermets

Influence of metallic binder content on the microhardness of TiCN-based cermet

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Load-Dependence of the Measured Hardness of Ti(C,N)-Based Cermets

Fracture Behaviors of Ti(C, N)-based Cermets with Different Contents of Metal Binder

Effect of Metallic Content on Mechanical Property of Ni/(10NiO-NiFe2O4) Cermets

Effect of Cr2C3 addition on microstructure and mechanical properties of Ti(CN)-based cermets

Effects of Process Parameters on Microstructure and Properties of TiC Reinforced Cu-Matrix Composites

The Effect of Carbon Content on the Microstructure and Mechanical Properties of Cemented Carbides with a CoNiFeCr High Entropy Alloy Binder

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

Effect of Cr<sub>2</sub>C<sub>3</sub> Addition on Microstructure and Mechanical Properties of Ti(CN)-Based Cermets

Effect of Copper Content on the Microstructures and Properties of Tib2 Based Cermets by Shs

Effect of binder content and sintering time on the microstructure and mechanical properties of gradient cemented carbides with Ni binder

Effect of Nano-Si3n4 Addition on the Microstructure and Mechanical Properties of Ticn-Based Cermets

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Effect of diamond addition on microstructure and mechanical properties of Ti(C,N)-based cermets

The effect of binder phase content on WC-AlCoCrFeNiTi0.2 high entropy cemented carbides microstructure and mechanical properties

Effect of In-situ Transformed Pre-oxidized Polyacrylonitrile Fibers on the Microstructure and Mechanical Properties of TiCN-based Cermets

TiCN Cermets with MnFeCoNiCu High Entropy Alloy Binder

Effect of the carbon content on the morphology evolution of the η phase in cemented carbides with the CoNiFeCr high entropy alloy binder

Effect of tungsten carbide content on the tribological behavior of TiB2–TiC-based cermets