Abstract:Large diameter thin-walled tubes are prone to wrinkle due to a low stability of anti-wrinkles, non-uniform material flow, and contact sequence to the die cavity during hydroforming process. Although wrinkling defects can be controlled by reducing the diameter of the initial tube to some extent, the severe thinning will occur. A method of using local constraints was proposed to eliminate wrinkling defects that occurred on thin-walled hydroformed tubes. The effect of axial constraint, hoop constraint, and axial-and-hoop constraint on wrinkling behavior of large diameter thin-walled tubes has been investigated by using numerical simulation and experiment methods. In addition, the trajectory of principal stress of the wrinkling zones with different local constraints has been discussed. The results show that axial compressive stress of the two wrinkling zones can be reduced by 6.8 and 23.0% by using axial constraint, respectively. Hoop constraint reduces axial compressive stress by 11.7% at the two wrinkling zones. And the axial compressive stress remarkably decreased by 22.3 and 31.8% using axial-and-hoop constraint. The results reveal that the application of local constraints can effectively restrict the occurrence of wrinkle by decreasing axial compressive stress during hydroforming of large diameter thin-walled tubes. Finally, a desired part without defects has been manufactured successfully by axial-and-hoop constraint.

Control and use of wrinkles in tube hydroforming

Research on wrinkling behavior in tube hydroforming

Effect of Wrinkling Behavior on Formability and Thickness Distribution in Tube Hydroforming

Deformation Patterns in Hydroforming of Thin-Walled Y-Shaped Tube

WRINKLING BEHAVIOR IN HYDROFORMING OF UNSYMMETRICAL TUBULAR PART

Analysis of Plastic Wrinkling Behavior in Tube Hydroforming Process

Wrinkling Behavior in Tube Hydroforming Coupled with Internal and External Pressure

Study on Wrinkling Behavior in Hydroforming of Large Diameter Thin-Walled Tube Through Local Constraints

Numerical simulation of wrinkling in hydroforming of aluminum alloy tubes

Analysis on wrinkling and cracking initiation in hydroforming thin?walled Y?shaped tubes

Thickness Improvement in Hydroforming of a Variable Diameter Tubular Component by Using Wrinkles and Preforms

Effect of Wrinkles on Formability in Hydroforming A Double-Diameter Aluminum Alloy Tubular Part

Research on Bursting Behavior in Hydroforming of Double-Cone Tube

A Study on Numerical Simulation of Hydroforming of Aluminum Alloy Tube

Analysis of Warping Failure in Tube Hydro-Forging

Analysis on Critical Conditions of Sidewall Wrinkling for Hydroforming of Thin-Walled Tee-Joint

Analysis on Corner Wrinkling for Axial Hydro-Forging of Variable-Diameter Tube

Wrinkling Behavior of Magnesium Alloy Tube in Warm Hydroforming

Investigation into the Pre-Forming'S Effect During Multi-Stages of Tube Hydroforming of Aluminum Alloy Tube by Using Useful Wrinkles

Experimental and Numerical Investigation into Useful Wrinkling During Aluminium Alloy Internal High-Pressure Forming

Wrinkle Analysis and Control of Tube Bending for Hydroforming