Preparation and Thermal Emission Characteristics of [Ca24Al28O64]4+:4e− Electronic Compounds
Lijun Cao,Yixin Xiao,Mingming Wang,Boyu Jiang,Xin Zhang,Wei Huang,Zhengyang Jin
DOI: https://doi.org/10.1007/s11664-024-11353-w
IF: 2.1
2024-10-02
Journal of Electronic Materials
Abstract:The [Ca 24 Al 28 O 64 ] 4+ :4e − electronic compounds (C12A7:e − ) with low work function and stable chemical properties have been employed in electron emission and optical devices. In this paper, C12A7:e − was successfully prepared using CaO, Al 2 O 3 , and Al powders through spark plasma sintering (SPS) at 1250°C for 20 min. The grain size of the sample does not exceed 10 μm. The sample exhibits typical Raman peaks at 175 cm −1 , 329 cm −1 , 510 cm −1 , 780 cm −1 , and a clear ultraviolet absorption peak at 2.6 eV. The carrier concentration of the sample reaches 1.67 × 10 21 cm −3 . The emission current density of the sample at 4000 V and 1100°C is 1.34 A/cm 2 , with a fluctuation of no more than 5%. The zero-field emission current density is 1.18 A/cm 2 at 1100°C. The lattice thermal conductivity of C12A7:e − decreases with increasing temperature, reaching 12.59 W/(K m) at 1100°C. In addition, the band structure of C12A7:e − includes valence band (VB), cage conduction band (CCB), and frame conduction band (FCB), and CCB extends to the Fermi level and has a bandgap of 0.82 eV with FCB. This makes C12A7:e − exhibit a typical band conduction mechanism. The electron emission characteristics of C12A7:e − are derived from the contributions of the s -orbital electrons of Ca atoms and the p -orbital and d -orbital electrons of Al atoms. This article simplifies the preparation steps of C12A7:e − cathode materials, shortens the synthesis cycle, and provides a foundation for the research of C12A7:e − cathode.
engineering, electrical & electronic,materials science, multidisciplinary,physics, applied