Abstract:Yttria-stabilized zirconia (YSZ) is a fine ceramics material that has been applied to dental implants and mechanical components. As YSZ is a hard, brittle, and chemically stable material, that undergoes phase transformation during mechanical loading, it is difficult to fabricate nanostructures using mechanical processing methods. In this study, a surface structuring method using a femtosecond pulsed laser was proposed, which is effective in suppressing the mechanical loading-induced phase transformation. As the material properties of YSZ vary with the concentration of yttria dopant , polycrystalline zirconia samples with different yttria concentrations (2, 3, 5, and 8 mol%) were used to investigate the effect of yttria concentrations on laser processing characteristics for nanostructuring. At all concentrations, nanopore generation in the surface grain was achieved by laser irradiation near the ablation threshold. In addition, there was no significant change in the crystal structure before and after laser irradiation, and no damage to the bulk occurred. At 2 mol%, intergranular cracks were generated around the pores. By increasing the dopant level to 5 mol%, the lens effect of the crystal grains became stronger due to enhanced grain growth, and the diameter and number of pores increased. In addition, pores formed preferentially on smaller grains at 5 mol%. However, for YSZ with 8 mol%, the pore formation phenomenon was different from that in the lower dopant level, as the area near the grain boundary was preferentially ablated, and microcracks formation and exfoliation of the surface also occurred. These results contribute to a deeper understanding of the laser ablation characteristics of zirconia with different dopant levels and to the development of surface structuring methods for fine ceramics materials.

Mechanical Properties and Microstructures of Sintered Zirconia Ceramics Implanted by Titanium Ions with MEVVA Sources

Study on comparision of the mechanical properties of ceramics after ion implantation

Hardness and Tribological Properties of Silicon Nitride Ceramics Implanted by Titanium Ions with MEVVA Sources

Bending Strength of Ceramics Implanted by Titanium, Zirconium and Chromium Ions with MEVVA Source

Study on the Properties of Alumina Ceramics after Implanted by Titanium Ions with MEVVA Sources

Structural and Conductive Changes of Alumina Ceramics and Silicon Crystal Implanted with High-Flux Ti Ion

Flexural Strength Change of Silicon Nitride Implanted by High Dose Titanium Ions

Nanoindentation Characterization of Tetragonal Zirconia Polycrystalline Implanted by Titanium Ions with MEVVA Sources

Mechanical Properties Of Zirconia Thin Films Deposited By Filtered Cathodic Vacuum Arc

Influence of Titanium Ions Implantation on Corrosion Behavior of Zirconium in 1M H2SO4

Effect of dopant concentration on femtosecond pulsed laser irradiation of yttria-stabilized zirconia for generating nanopores

Influence of Xe+ ion implantation on spectral properties of yttria-stabilized zirconia single crystals

Influence of ion implantation on properties and structure of silicon nitride

Influence of titanium ions implantation on corrosion behavior of zircaloy-2 in 1M H 2 SO 4

Microstructural modifications induced in Si+-implanted yttria-stabilised zirconia: a combined RBS-C, XRD and Raman investigation

Densification, microstructure, and nanomechanical evaluation of pulsed electric sintered zirconia-silicon nitride reinforced Ti-6Al-4 V alloy

Structure and fracture behavior of ion-beam-modified SiC-Al2O3-ZrO2 ceramic composites

Influence of Crystal Inducing Agent on the Phase Structure and Optical Properties of Nano Zirconia

The air oxidation of yttrium ion implanted zircaloy-4 at 500°C

Mechanical Performance of Polymer-Infiltrated Zirconia Ceramics.

The Influence of Yttrium Ion Implantation on the Oxidation Behavior of Zircaloy-4 at 600 °C