Abstract:Zircaloy-2 specimens were implanted with carbon ions in the fluence range from 1×1016 to 1×1018 ions/cm2, using a MEVVA source at an extraction voltage of 40 kV at a maximum temperature of 380 °C. The valences and depth profiles of elements in the implanted surface of Zircaloy-2 were analyzed by X-ray photoelectron spectroscopy and Auger electron spectroscopy, respectively. Scanning electron microscopy was used to examine the micro-morphology of samples. The color of the oxidized samples was checked with an optical scanner. Glancing-angle X-ray diffraction at 0.3° incident angles was employed to examine the phase transformations of implanted samples before and after oxidation in the air at 500 °C for 2 h. Before oxidation, at fluences less than 5×1016 ions/cm2, hexagonal zirconia (H-ZrO0.35) was present. At a fluence of 1×1017 ions/cm2, rhombohedral zirconia (R-Zr3O) appeared. When the fluence reached 1×1018 ions/cm2, cubic zirconium carbide was produced. There are many pits, both deep and shallow, in the sample surfaces, both prior to oxidation and after oxidation. Oxidation in the air at 500 °C gave rise to black surfaces on all samples. The X-ray diffraction results showed that monoclinic and tetragonal zirconia were present in the surface of as-received sample. For implanted samples, monoclinic and tetragonal zirconia are still present, while cubic zirconium carbide is produced at all fluences. The presence of ZrC is attributed to the high-temperature, long-time (2 h) exposure.

The Influence of Yttrium Ion Implantation on the Oxidation Behavior of Zircaloy-4 at 600 °C

The air oxidation of yttrium ion implanted zircaloy-4 at 500°C

Influence of Titanium Ion Implantation on the Corrosion Behavior of Zircalloy-4 in 1 M H2SO4

Surface analysis of Zircaloy-2 implanted with carbon before and after oxidation in air at 500 °C

High-temperature Oxidation of Sprayed Alumina and Zirconium‑yttrium-Based Coatings on Zircaloy-4 in Air and Oxygen: Investigation on Microstructure Evolution and Phase Changes

Assessment of microstructure, mechanical and tribological properties of Zr-4 alloy after pre-oxidation and ion irradiation

An in-situ TEM investigation of microstructure evolution in Cr-coated zirconium alloy under heavy ion irradiation: Simultaneous evolution of both Cr coating and Zr-4 matrix

Study of Oxidation Behavior and Associated Microstructure Evolution of Zircaloy-4 Exposed to High Temperature Pure Steam

Influence of Titanium Ions Implantation on Corrosion Behavior of Zirconium in 1M H2SO4

Influence of Aluminum Ions Implanted on Oxidation Behavior of ZIRLO Alloy at 500 °C

Insights into 1200 °C steam oxidation behavior of Cr coatings with different microstructure on Zircaloy-4 alloys for enhanced accident tolerant fuel cladding

New insights into the mechanism of yttrium changing high-temperature oxide growth of Fe-13Cr–6Al–2Mo–0.5Nb alloy for fuel cladding

The Effect of Y-ion Implantation on the Oxidation of AZ31 Magnesium Alloy

Influence of titanium ions implantation on corrosion behavior of zircaloy-2 in 1M H 2 SO 4

High-temperature steam oxidation experiment of molten zirconium alloy

Behavior of Implanted Strontium in Yttria-Stabilized Zirconia

Effect of Proton and Ne Irradiation on the Microstructure of Zircaloy 4

Transient Experiments on Oxidation and Degradation of Cr-coated Zircaloy in Steam Up to 1600 ℃

Modification of Corrosion Resistance by Yttrium Ion Implantation of 30 4L Stainless Steel

Influence of ions irradiation on the microstructural evolution, mechanical and tribological properties of Zr-4 alloy

Lattice damage and secondary phase formation in yttria stabilised zirconia implanted with Fe at different temperatures