Surface analysis of Zircaloy-2 implanted with carbon before and after oxidation in air at 500 °C

D PENG,X BAI,F PAN,H SUN,B CHEN

DOI: https://doi.org/10.1016/j.matchar.2005.09.016

IF: 4.537

2006-01-01

Materials Characterization

Abstract:Zircaloy-2 specimens were implanted with carbon ions in the fluence range from 1×1016 to 1×1018 ions/cm2, using a MEVVA source at an extraction voltage of 40 kV at a maximum temperature of 380 °C. The valences and depth profiles of elements in the implanted surface of Zircaloy-2 were analyzed by X-ray photoelectron spectroscopy and Auger electron spectroscopy, respectively. Scanning electron microscopy was used to examine the micro-morphology of samples. The color of the oxidized samples was checked with an optical scanner. Glancing-angle X-ray diffraction at 0.3° incident angles was employed to examine the phase transformations of implanted samples before and after oxidation in the air at 500 °C for 2 h. Before oxidation, at fluences less than 5×1016 ions/cm2, hexagonal zirconia (H-ZrO0.35) was present. At a fluence of 1×1017 ions/cm2, rhombohedral zirconia (R-Zr3O) appeared. When the fluence reached 1×1018 ions/cm2, cubic zirconium carbide was produced. There are many pits, both deep and shallow, in the sample surfaces, both prior to oxidation and after oxidation. Oxidation in the air at 500 °C gave rise to black surfaces on all samples. The X-ray diffraction results showed that monoclinic and tetragonal zirconia were present in the surface of as-received sample. For implanted samples, monoclinic and tetragonal zirconia are still present, while cubic zirconium carbide is produced at all fluences. The presence of ZrC is attributed to the high-temperature, long-time (2 h) exposure.