Abstract:To investigate the microstructural evolution during high temperature oxidation, Cr-coated Zr-4 alloy specimens are prepared by multi-arc ion plating and high temperature oxidation tests are carried out under 1000°C, 1100°C and 1200°C in air atmosphere. Cr2O3 layers are formed on the surface after high temperature oxidation test. However, the thickness of Cr2O3 layer does not depend monotonously on the oxidation temperature. The oxidation temperature increases from 1000°C to 1100°C, the thickness of Cr2O3 layer increases from 2.35 μm to 5.74 μm, while the thickness is only 4.1 μm when the oxidation temperature is 1200°C. This is mainly due to the reduction of Cr2O3 to Cr, and oxygen diffuses into the substrate to form α-Zr. The oxidation weight gain for the three temperatures conforms to an exponential function, while the thickness of the Cr-Zr diffusion layers follows a linear relationship with the oxidation temperature. Regarding the Zr-4 alloy substrate, the Zr grains grow up and gradually change from elongated grain parallel to the interface to elongated grain along normal direction after high temperature oxidation. Moreover, different oxidation temperatures bring distinct recrystallization energy to Zr grains, and the defects and dislocations produced during the recrystallization of Zr grain are unequal. The kernel average misorientation values obtained from EBSD indicate that the overall density of defect and dislocation of Zr grains after high temperature oxidation under 1100°C is higher than the other two temperatures, while Zr grains after high temperature oxidation under 1000°C has the highest local density of defect and dislocation. The investigation in this study attempts to reveal the microstructure evolution of Cr coating and Zr-4 substrate during the high temperature oxidation. These results give some new perspectives on understanding the performance of Cr-coated Zr-4 alloy under high temperature environment.

Microstructural evolution of pre-oxidized Cr-coated Zry-4 during annealing in argon

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Microstructural evolution of Cr-coated Zr-4 alloy prepared by multi-arc ion plating during high temperature oxidation

Systematic Investigations on the Coating Degradation Mechanism During the Steam Oxidation of Cr-coated Zry-4 at 1200 °C

Microstructure Evolution of a Cr-Cr/Mo Coated Zr Alloys in Inert Gas and Steam Environment at High Temperature

Steam Oxidation Of Cr-Coated Sn-Containing Zircaloy Solid Rod At 1000 Degrees C

Microstructure evolution and high temperature air oxidation behaviour of thick Cr coatings at 1200°C

Microstructural Evolution of Irradiated Cr-Coated Zr-4 under In Situ Transmission Electron Microscopy Heating

In-situ Observation of Microstructure Evolution of Cold Sprayed CrZrCu Alloy Coating During Heating

Steam oxidation of Cr-coated zirconium alloy claddings at 1200 °C: Kinetics transition and failure mechanism of Cr coatings

In-situ study on the microstructure and cracking behavior of annealed Cr coated Zr-4 alloy

Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam

The effect of short-term annealing in an Ar environment on microstructure and adhesion property of Cr-coated Zircaloy-4 claddings

Reducing the Oxidation Rate of Cr-coated Zr Alloys under High Temperature Steam Environment: an Approach of an Outer Zr Coating

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions

High-temperature Oxidation of Sprayed Alumina and Zirconium‑yttrium-Based Coatings on Zircaloy-4 in Air and Oxygen: Investigation on Microstructure Evolution and Phase Changes

Steam oxidation of Cr-coated Sn-containing Zircaloy solid rod at 1000 °C

Microstructural Understanding of CrN Layer As a Barrier Against Cr-Zr Interdiffusion in Cr-coated Zirconium Alloy for Accident Tolerant Fuel Claddings

Microstructure evolution and oxidation behavior of bi-layer CrAl-Mo coated Zircaloy-4 in steam at 1200 o C and 1300 o C

High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

The high-temperature oxidation and mechanical properties of the Cr/Zr and CrN/Zr coating