Abstract:The microstructure developed in Zr alloys during irradiation has proven to be increasingly complicated as specimens of varying composition and thermo-mechanical history have been irradiated to higher fluences.Cavities form in neutron and electron irradiated Zr at temperatures between 625 and 775 K. They are less common in the Zircaloys either because of vacancy trapping or because c-component dislocation loops compete for vacancies. There is a complex dependence on the purity of the material which is related to the presence of precipitates or interstitial solutes and on the presence of insoluble gases such as He. The latter is necessary to prevent the collapse of small vacancy clusters to form vacancy loops.Vacancy and interstitial dislocation loops having Burgers vectors of b =13〈112̄0〉 (〈a〉 type) coexist during neutron and electron irradiation. They are generally aligned in rows or layers parallel with (0001). There is a marked decrease in the stability of vacancy 〈a〉 type loops at temperatures ⩾ 723K. Dislocation loops having Burgers vectors of b = 12[0001] (vacancy type), b = 13〈112̄3〉 (interstitial type) and 16〈202̄3〉 (undetermined character) have been identified in Zr following electron irradiation at temperatures between 573–773 K. Vacancy loops of b = 16〈202̄3〉 have been observed in Zr and Zr alloys with a high interstitial solute content following neutron irradiation at temperatures between 560–773 K. Their formation and growth is determined by a combination of: (i) size effect interaction, dependent on their Burgers vector; (ii) stress, generated in collision cascades during neutron irradiation or in oxidised thin foils during electron irradiation; (iii) interstitial solute, which may lower the stacking-fault energy or segregate to the dislocations bounding the loops; and (iv) anisotropic interstitial diffusion (principally in the basal plane).The dislocation network in cold-worked materials is retained during neutron irradiation, at least for fluences up to 7 × 1025 n m−2 at 573 K. Intermetallic precipitates of Zr with Fe, Cr and Ni undergo amorphous transformations (depending on the precipitate composition) during neutron irradiation at temperatures < 600 K. Radiation-induced dissolution and reprecipitation occurs at temperatures > 560 K. The secondary precipitates are often distributed in rows or layers parallel with (0001). Radiation-enhanced precipitation from solution has been observed in ZrSn and ZrNb alloys at temperatures between about 573–873 K.

Microstructural Evolution of Irradiated Cr-Coated Zr-4 under In Situ Transmission Electron Microscopy Heating

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

An in-situ TEM investigation of microstructure evolution in Cr-coated zirconium alloy under heavy ion irradiation: Simultaneous evolution of both Cr coating and Zr-4 matrix

Surface Growth, Inner Defects and Interface Mixing of the Cr Coating on Zr Alloy Irradiated by 5 Mev Protons at 400 °C

Surface growth, inner defects and interface mixing of Cr coating on Zr alloy irradiated by 5 MeV protons at 400°C

Cr-coated Zr-4 alloy prepared by electroplating and its in situ He+ irradiation behavior

Microstructural evolution of pre-oxidized Cr-coated Zry-4 during annealing in argon

In Situ TEM Study of Microstructure Evolution of Zr-Nb-Fe Alloy Irradiated by 800 keV Kr2+ Ions

Microstructure evolution and interdiffusion behaviour of Cr/Mo coated Zr-4 alloys at 1330 °C-1500 °C

Microstructural evolution of Cr-coated Zr-4 alloy prepared by multi-arc ion plating during high temperature oxidation

Tem Characterizations of a Zro2/Cr Composite Coating on Zr-1nb Alloy after 1200°C Steam Oxidation

Evolution of microstructure and mechanical properties of ZrC reinforced FeCrAl alloy after Fe-ions irradiation

Microstructure evolution and adhesion properties of thick Cr coatings under different thermal shock temperatures

Effect of Proton and Ne Irradiation on the Microstructure of Zircaloy 4

Microstructure evolution and high temperature air oxidation behaviour of thick Cr coatings at 1200°C

Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam

Microstructure Evolution of V2alc Coating on Zr Substrate under He Irradiation and Their Mechanical Behavior

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions

Steam Oxidation Of Cr-Coated Sn-Containing Zircaloy Solid Rod At 1000 Degrees C

Evolution of structures and internal stress of ZrC-SiC composite under He ion irradiation and post-annealing

A review of microstructure evolution in zirconium alloys during irradiation