Abstract:Cr 3 Si and Cr coatings were deposited on Zry-4 substrates via magnetron sputtering to examine their oxidation behavior in steam ranging from 1200 to 1400 °C. At 1200 °C, a dense Cr 2 O 3 layer that formed on the surface of the Cr 3 Si-coated Zry-4 followed a power-law function, preventing the internal diffusion of O. Additionally, an in-situ Zr 2 Si layer, developed between the Cr 3 Si coating and Zry-4 substrate, significantly mitigated the outward diffusion of Zr. However, at 1330 °C in steam, the continuity of the Zr 2 Si layer was disrupted due to the formation of ZrCr 2 , which facilitated the outward diffusion of Zr to the interface between the remaining Cr 3 Si layer and the outer Cr 2 O 3 layer. Despite the reduction in the Cr 2 O 3 layer thickness caused by redox reactions between Cr 2 O 3 and Zr, the Cr 3 Si coating still managed to delay the steam oxidation of the Zry-4 substrate for over 60 min at 1330 °C. While on the uncoated side, the thickness of the formed ZrO 2 reached 846 ± 5.2 μm. For the Cr coating, after 30 min of oxidation in steam at 1330 °C, a significant liquid eutectic formed between the Cr coating and the Zry-4 substrate, compromising the coating's overall structural stability. The oxidation resistance of the Cr 3 Si coating surpasses that of the Cr coating after exposure to steam at 1400 °C for 10 min. These findings suggest that the Cr 3 Si coatings hold promise for robustly protecting zirconium alloy cladding in scenarios involving design basis accidents (DBA) and beyond design basis accidents (BDBA).

Growth kinetics and microstructure characteristics of the Zr-Cr interlayer in a Cr-coated Zry-4 alloy exposed to high-temperature steam

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions

Steam oxidation of Cr-coated zirconium alloy claddings at 1200 °C: Kinetics transition and failure mechanism of Cr coatings

Investigation of oxidation behaviors of bi-layer CrAl-Cr coated Zircaloy-4 in steam at 1300 oC

Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam

Oxidation behavior, thermal stability, and the coating/substrate interface evolution of CrN-coated Zircaloy under high-temperature steam

Microstructure evolution and oxidation behavior of bi-layer CrAl-Mo coated Zircaloy-4 in steam at 1200 o C and 1300 o C

Improved oxidation resistance of Cr/FeCrAl coating on Zr alloy in high-temperature steam environment

Tem Characterizations of a Zro2/Cr Composite Coating on Zr-1nb Alloy after 1200°C Steam Oxidation

Systematic investigations on the microstructural evolution and degradation mechanism of Cr 3 Si-coated Zry-4 under DBA and BDBA conditions

Steam Oxidation Of Cr-Coated Sn-Containing Zircaloy Solid Rod At 1000 Degrees C

Investigation on Microstructures and High-Temperature Oxidation Resistance of Cr Coatings on Zircaloy-4 by Multi-Arc Ion Plating Technology

Study on eutectic-oxidation coupling reaction of Cr-Zr system in high temperature steam environment

Investigation Of The Oxidation Mechanisms Of Superlattice Cr-Crn/Tisin-Cr Multilayer Coatings On Zircaloy Substrates Under High-Temperature Steam Atmospheres

High-Temperature Steam Oxidation of Accident-Tolerant Cr/Mo-Coated Zr Alloy at 1200–1400 °C

Isothermal experiments on steam oxidation of magnetron-sputtered chromium-coated zirconium alloy cladding at 1200 °C

High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

Degradation of the Cr 2 O 3 layer protectiveness caused by grain refinement during high-temperature oxidation of Cr coatings

Long‐term high‐temperature steam oxidation behavior of Cr‐coated Zircaloy‐4 alloy for accident tolerant fuel

Steam oxidation of Cr-coated Sn-containing Zircaloy solid rod at 1000 °C