Abstract:To investigate the microstructural evolution during high temperature oxidation, Cr-coated Zr-4 alloy specimens are prepared by multi-arc ion plating and high temperature oxidation tests are carried out under 1000°C, 1100°C and 1200°C in air atmosphere. Cr2O3 layers are formed on the surface after high temperature oxidation test. However, the thickness of Cr2O3 layer does not depend monotonously on the oxidation temperature. The oxidation temperature increases from 1000°C to 1100°C, the thickness of Cr2O3 layer increases from 2.35 μm to 5.74 μm, while the thickness is only 4.1 μm when the oxidation temperature is 1200°C. This is mainly due to the reduction of Cr2O3 to Cr, and oxygen diffuses into the substrate to form α-Zr. The oxidation weight gain for the three temperatures conforms to an exponential function, while the thickness of the Cr-Zr diffusion layers follows a linear relationship with the oxidation temperature. Regarding the Zr-4 alloy substrate, the Zr grains grow up and gradually change from elongated grain parallel to the interface to elongated grain along normal direction after high temperature oxidation. Moreover, different oxidation temperatures bring distinct recrystallization energy to Zr grains, and the defects and dislocations produced during the recrystallization of Zr grain are unequal. The kernel average misorientation values obtained from EBSD indicate that the overall density of defect and dislocation of Zr grains after high temperature oxidation under 1100°C is higher than the other two temperatures, while Zr grains after high temperature oxidation under 1000°C has the highest local density of defect and dislocation. The investigation in this study attempts to reveal the microstructure evolution of Cr coating and Zr-4 substrate during the high temperature oxidation. These results give some new perspectives on understanding the performance of Cr-coated Zr-4 alloy under high temperature environment.

Microstructure evolution and oxidation behavior of bi-layer CrAl-Mo coated Zircaloy-4 in steam at 1200 o C and 1300 o C

Investigation of oxidation behaviors of bi-layer CrAl-Cr coated Zircaloy-4 in steam at 1300 oC

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Influence of Al content on the oxidation behavior of CrAl coating on Zry-4 alloys in 1200 °C steam

High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

Improved oxidation resistance of Cr/FeCrAl coating on Zr alloy in high-temperature steam environment

High temperature oxidation of CrAl-coated Zr–1 Nb alloy in 1000 – 1300 °C steam

Oxidation behavior of CrAl-Mo coated Zircaloy-4 in DB and BDB scenarios

Microstructure evolution and high temperature air oxidation behaviour of thick Cr coatings at 1200°C

High-Temperature Steam Oxidation of Accident-Tolerant Cr/Mo-Coated Zr Alloy at 1200–1400 °C

Microstructure evolution and interdiffusion behaviour of Cr/Mo coated Zr-4 alloys at 1330 °C-1500 °C

Investigation of oxidation behaviors of coated Zircaloy as accident-tolerant fuel with CrAlN and CrAlSiN coatings in high-temperature steam

Effect of Cr/Al Atomic Ratio on the Oxidation Resistance in 1200°C Steam for the CrAlSiN Coatings Deposited on Zr Alloy Substrates

Effect of Al content on 1200 °C steam oxidation behavior of Cr-based coatings on TZM alloy

High-Temperature Oxidation And Tensile Behaviors Of Cral Coating On Zirconium Alloy

Insights into 1200 °C steam oxidation behavior of Cr coatings with different microstructure on Zircaloy-4 alloys for enhanced accident tolerant fuel cladding

Microstructural evolution of Cr-coated Zr-4 alloy prepared by multi-arc ion plating during high temperature oxidation

Isothermal experiments on steam oxidation of magnetron-sputtered chromium-coated zirconium alloy cladding at 1200 °C

Investigation on Microstructures and High-Temperature Oxidation Resistance of Cr Coatings on Zircaloy-4 by Multi-Arc Ion Plating Technology

Steam oxidation of Cr-coated zirconium alloy claddings at 1200 °C: Kinetics transition and failure mechanism of Cr coatings

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions