Abstract:To investigate the microstructural evolution during high temperature oxidation, Cr-coated Zr-4 alloy specimens are prepared by multi-arc ion plating and high temperature oxidation tests are carried out under 1000°C, 1100°C and 1200°C in air atmosphere. Cr2O3 layers are formed on the surface after high temperature oxidation test. However, the thickness of Cr2O3 layer does not depend monotonously on the oxidation temperature. The oxidation temperature increases from 1000°C to 1100°C, the thickness of Cr2O3 layer increases from 2.35 μm to 5.74 μm, while the thickness is only 4.1 μm when the oxidation temperature is 1200°C. This is mainly due to the reduction of Cr2O3 to Cr, and oxygen diffuses into the substrate to form α-Zr. The oxidation weight gain for the three temperatures conforms to an exponential function, while the thickness of the Cr-Zr diffusion layers follows a linear relationship with the oxidation temperature. Regarding the Zr-4 alloy substrate, the Zr grains grow up and gradually change from elongated grain parallel to the interface to elongated grain along normal direction after high temperature oxidation. Moreover, different oxidation temperatures bring distinct recrystallization energy to Zr grains, and the defects and dislocations produced during the recrystallization of Zr grain are unequal. The kernel average misorientation values obtained from EBSD indicate that the overall density of defect and dislocation of Zr grains after high temperature oxidation under 1100°C is higher than the other two temperatures, while Zr grains after high temperature oxidation under 1000°C has the highest local density of defect and dislocation. The investigation in this study attempts to reveal the microstructure evolution of Cr coating and Zr-4 substrate during the high temperature oxidation. These results give some new perspectives on understanding the performance of Cr-coated Zr-4 alloy under high temperature environment.

Oxidation kinetics of Cr-coated zirconium alloy: Effect of coating thickness and microstructure

Oxidation Behavior of Cr-coated Zirconium Alloy Cladding in High-Temperature Steam above 1200 °C

High-temperature oxidation of Zr 1Nb zirconium alloy with protective Cr/Mo coating

Steam oxidation of Cr-coated zirconium alloy claddings at 1200 °C: Kinetics transition and failure mechanism of Cr coatings

The high-temperature oxidation and mechanical properties of the Cr/Zr and CrN/Zr coating

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions

Microstructural evolution of Cr-coated Zr-4 alloy prepared by multi-arc ion plating during high temperature oxidation

Isothermal experiments on steam oxidation of magnetron-sputtered chromium-coated zirconium alloy cladding at 1200 °C

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Mechanical and high-temperature steam oxidation properties of Cr coatings deposited via high-power impulse magnetron sputtering

High-Temperature Oxidation And Tensile Behaviors Of Cral Coating On Zirconium Alloy

High-Temperature Steam Oxidation of Accident-Tolerant Cr/Mo-Coated Zr Alloy at 1200–1400 °C

Oxidation Behavior and Kinetics of Magnetron-sputtered Cr-coated Zr Alloy Cladding in 1000~1300°C Steam Environment

Effect of Diffusion Barriers on Steam Oxidation Properties and Interface Evolutions of Cr Coating for Zirconium Alloy at 1200 °C

Microstructure evolution and high temperature air oxidation behaviour of thick Cr coatings at 1200°C

Oxidation Behavior of Cr1-xAlx Coated Zr-4 Alloy under 1200 °C High Temperature Steam Environment

Microstructure evolution and oxidation behavior of bi-layer CrAl-Mo coated Zircaloy-4 in steam at 1200 o C and 1300 o C

Molybdenum Texture Effect on High Temperature Oxidation Resistance of Cr/Mo-Coated Zr–1Nb Alloy

Effect of Molybdenum Texture on the High-Temperature Oxidation Resistance of Zr–1Nb Alloy with a Cr/Mo Coating

Systematic Investigations on the Coating Degradation Mechanism During the Steam Oxidation of Cr-coated Zry-4 at 1200 °C

Reducing the Oxidation Rate of Cr-coated Zr Alloys under High Temperature Steam Environment: an Approach of an Outer Zr Coating