Abstract:Abstract Nitrides, carbides, and carbonitrides of transition metal elements like Zr, W, Ti, etc. are generally employed to produce hard coatings. Zirconium-based hard coatings have shown useful applications in the areas of tribology, biomedicine and electrical due to their high thermal stability, hardness, biocompatibility, good erosion, wear, and corrosion resistance. In this study, we created homogeneous and tenacious nanostructured hard coatings based on Zr with good mechanical properties. The magnetron sputter deposition technique was utilized to coat stainless steel 316L substrates with multilayers of Zr/ZrN and ZrN/ZrCN with individual layer thicknesses of 250 and 500 nm for each coating composition. The deposition conditions were adjusted to create two different coating thicknesses of 2 and 3 μm. The thickness of the coating was confirmed using Calotest and the coatings’ morphology and elemental composition were determined utilizing the atomic force microscope and scanning electron microscope equipped with energy dispersive x-ray spectrometer. Coating thickness and adhesion were measured using cross-sectional samples and XRD was utilized to analyze the coatings structure. Nanoindenter was employed to determine the instrumental nanoindentation hardness and elastic modulus. The influence of coating thickness on tribological behavior was further investigated using the ratio of nanohardness-to-elastic modulus (H/E). No evidence of decohesion was observed at the substrate/coatings interface, and the grains of all the coatings were observed to show columnar growth which were homogeneous, compact and dense. The grains of the ZrN/ZrCN coatings were observed to be denser, finer and more compact compared to those of the Zr/ZrN coatings. Correspondingly, higher hardness, modulus and H/E values were exhibited by ZrN/ZrCN than Zr/ZrN coatings. This suggests that the ZrN/ZrCN coatings are capable of exhibiting better wear resistance and fracture toughness. The coatings developed in this investigation are anticipated to be suitable for applications in tribology due to their excellent hardness and H/E properties.

Fretting wear behavior of nitrogen implanted Zircaloy-4 alloy

Influence of ions irradiation on the microstructural evolution, mechanical and tribological properties of Zr-4 alloy

Nitrogen Ion Implantation on the Mechanical Properties of Aisi 420 Martensitic Stainless Steel

Wear Behavior of Zirconium-4 Alloy after Different Irradiation Damage Level

Improvement of nitrogen ion implantation on the wear and corrosion resistance of bearing steel in NaCl solution

Fretting wear behaviors of Zr-4 alloy under different ions irradiation conditions

MODIFICATION OF TRIBOLOGICAL CHARACTERISTICS OF METALS AFTER NITROGEN IMPLANTATION

Surface analysis of Zircaloy-2 implanted with carbon before and after oxidation in air at 500 °C

Deposition, microstructure and nanoindentation of multilayer Zr nitride and carbonitride nanostructured coatings

Hardness and Tribological Properties of Silicon Nitride Ceramics Implanted by Titanium Ions with MEVVA Sources

Interface-controlled mechanical properties and irradiation hardening in nanostructured Cr75Al25/Zr multilayers

Flexural Strength Change of Silicon Nitride Implanted by High Dose Titanium Ions

Irradiation simulation of zirconium using high energy argon implantation

Surface Analysis of Zirlo Alloy Implanted with Carbon

Irradiation Damage Simulation of Zircaloy-4 Using Argon Ions Bombardment

The Cavitation Erosion of the 45# Carbon Steels Implanted with Titanium and Nitrogen

Microstructure and wear behavior of inductive nitriding layer in Ti–25Nb–3Zr–2Sn–3Mo alloys

Characterization and fretting wear behavior of zirconium alloy treated in high temperature water

A Study Of Zrn/Zr Coatings Deposited On Niti Alloy By Piiid Technique

Microstructures and properties of (TiCrZrVAl)N high entropy ceramics films by multi-arc ion plating

Assessment of microstructure, mechanical and tribological properties of Zr-4 alloy after pre-oxidation and ion irradiation